| Density (g/cm³) |
ISO 1183 |
0.960 |
| Melt Flow Rate at 190 °C and 5.0 kg (g/10 min) |
ISO 1133 |
0.20 |
| Tensile Strength at Yield (MPa) |
ASTM D 638 @ Crosshead speed 50 mm/min |
24 |
| Tensile Strength at Yield (MPa) |
ISO 527 |
24 |
| Tensile strength at Break (MPa) |
ISO 527 |
> 30 |
| Elongation at Break (%) |
ISO 527 |
> 600 |
| Flexural Modulus (MPa) |
ASTM D 790 |
1,000 |
| Carbon black dispersion (Grading) |
ISO 18553 |
<3 |
| Carbon black content (%wt) |
ISO 6964 |
2.25 |
| Oxidative induction time at 210°C (min) |
ISO 11357 |
≥ 50 |
| MRS classification (MPa) |
ISO 12162/ISO 9080 |
11.2 |
| Resistance to slow crack growth at 80°C (hrs) |
ISO 13479 |
> 1,000 |
| Rapid crack propagation Pc, S4 (bar) |
ISO 13477 |
> 10 |
| Resistance to gas constituents (hrs) |
ISO 1167 |
> 25 |