EL-Lene™ D311C is an autoclave LDPE grade for extrusion coating/lamination with excellent neck in performance and outstanding organoleptic.
แอลดีพีอี
ทั้งหมด 4 เกรด
EL-Lene™ LDPE is a low-density polyethylene resin produced by an autoclave process, a technology developed by ICI Co., Ltd. of England.
| แอลดีพีอี (4) | Density (g/cm3) | Melt Index at 190 °C and 2.16 kg (g/10 min) | |||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| D311C | 0.915 | 7 | - | ||||||||||||||||||||||
| TDS | SDS | โบรชัวร์ | |||||||||||||||||||||||
|
คำอธิบาย
EL-Lene™ D311C is an autoclave LDPE grade for extrusion coating/lamination with excellent neck in performance and outstanding organoleptic. ผลิตภัณฑ์สำเร็จรูปที่เกี่ยวข้อง
-
|
|||||||||||||||||||||||||
| D388C | 0.917 | 8 | - | ||||||||||||||||||||||
| TDS | SDS | โบรชัวร์ | |||||||||||||||||||||||
|
คำอธิบาย
EL-Lene™ D388C is an autoclave LDPE grade for high speed extrusion coating/lamination with good processibility and organoleptic.
|
|||||||||||||||||||||||||
| D477C | 0.922 | 4 | - | ||||||||||||||||||||||
| TDS | SDS | โบรชัวร์ | |||||||||||||||||||||||
|
คำอธิบาย
EL-Lene™ D477C is an autoclave LDPE grade for extrusion coating/lamination with good stiffness and neck in performance.
ผลิตภัณฑ์สำเร็จรูปที่เกี่ยวข้อง
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
|
|||||||||||||||||||||||||
| D777C | 0.918 | 7 | - | ||||||||||||||||||||||
| TDS | SDS | โบรชัวร์ | |||||||||||||||||||||||
|
คำอธิบาย
EL-Lene™ D777C is an autoclave LDPE grade for extrusion coating/lamination with excellent processsability and good organoleptic.
ผลิตภัณฑ์สำเร็จรูปที่เกี่ยวข้อง
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
|
|||||||||||||||||||||||||