SCGC™ LLDPE D682PC is a black linear low density polyethylene compound. Well dispersed carbon black creates outstanding UV resistance and thermal stability.

Properties	Test Methods	Value
Density (g/cm³)	ISO 1183	0.946
Melt Flow Rate at 190 °C and 2.16 kg (g/10 min)	ISO 1133	0.24
Tensile Strength at Yield (MPa)	ASTM D 638 @ Crosshead speed 50 mm/min	17
Tensile Strength at Yield (MPa)	ISO 527	17
Tensile strength at Break (MPa)	ISO 527	> 30
Elongation at Break (%)	ISO 527	> 600
Carbon black content (%wt)	ISO 6964	2.25
Oxidative induction time at 210°C (min)	ISO 11357	≥ 40

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P403J is a homopolymer polypropylene resin suitable for general propose product which required good impact resistance produced from injection molding process.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P441JU is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires good outdoor performance.

SCGC™ PP P483JU is a developmental of high stiffness polypropylene impact copolymer product which contains anti-static agent and UV stabilizer. It is designed for very high stiffness, creep resistance, and high heat resistance while maintain a good impact strength than those of general impact copolymer polypropylene and suitable for injection molding application.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P642J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is suitable for Injection molding process. This resin is recommended for product that requires high impact strength and stiffness.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P700J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process from SCG.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P722JO is polypropylene impact copolymer which contains UV stabilizer. This resin is recommended for producing battery case from injection molding process.

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P840J is a high flow ability impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P841J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires very high processability and good UV performance.

SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC™ PP P851JO is a random copolymer polypropylene resin which giving high clarity, high brightness, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ SMX551BU is a high strength polyethylene produced by SMX™ technology suitable for Intermediate Bulk Containers. This grade provides high melt strength for good processing performance, very low odor and fuming and excellent chemical resistance with superior stiffness.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

3985 is a color compound high density polyethylene which exhibits superior mechanical properties when compared to traditional high density grades. This grade has been specifically developed for kayaks and for products that require a combination of high impact strength and rigidity. 3985 is fully UV stabilized with a minimum UV8 rating.

10901CLA is a non-PVC compound based on polyolefin raw materials. The product is designed for continuous compression molding and specially formulated for using as a gasket material in metal crowns for beverage applications.

10901WHA is a non-PVC compound based on polyolefin raw materials. The product is designed for continuous compression molding and specially formulated for using as a gasket material in metal crowns for beverage applications.

10908WHA is a thermoplastic elastomer based on polyolefin raw materials. The product is designed for continuous compression molding and specially formulated for using as a gasket material in aluminium closures.

17801WHA is a non-PVC compound based on polyolefin raw materials. The product is designed for continuous compression molding and specially formulated for using as a gasket material in metal crowns for filling goods like soybean milk.

17804WHE is a non-PVC compound based on polyolefin raw materials. The product is designed for continuous compression molding and specially formulated for using as a gasket material in Roll-on-pilfer-proof (ROPP) caps for filling goods like soybean milk.

SCGC GREEN POLYMER™ BWO1501G is a water-based barrier coating agent, providing a tailor-made oxygen barrier level with achievable Oxygen Transmission Rate (OTR) of less than 1 cc/m2*day and good adhesion for various plastic substrates

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE F15 is a high density polyethylene product of bi-modal process. It is recommended for film which is produced by high speed machine and wide lay flat. The key characteristics are high tesile strength and high productivity.

SCGC™ HDPE H1000PBL is a blue (no lighter than RAL 5005), bimodal, high density polyethylene compound that is specially designed for water pressure pipe, especially for drinking water pipe. SCGC™ HDPE H1000PBL is designed as PE100 pipe providing excellent in mechanical properties, and processablitiy. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term using.

SCGC™ HDPE H1000PC is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PCI is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. It is particularly designed for injection molding for pipe fittings.In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PWI is a white HDPE compound made for external coating on SCGC™ HDPE H1000PC for above ground pipe applications. It provides high mechanical properties, good processability, and low heat absorption. In addition the good dispersion and high concentration of stabilizers contribute excellent long term UV resistance and thermal stability.

SCGC™ HDPE H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology. SCGC™ HDPE H112PC is classified as MRS 11.2 material (PE112). It provides superior long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides that, it can be produced in all ranges of pipe diameters, especially recommended for the production of very thick wall and large diameter pipe.

SCGC™ HDPE H2001WC is a black bimodal high density polyethylene compound for jacketing in fiber optic and power cable applications. It contains well-dispersed carbon black to provide excellent weathering and UV resistance.

SCGC™ HDPE H355JA is a high density polyethylene resin with good processability, good mechanical and excellent organoleptic properties, designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H377C is a bi-modal high density polyethylene resin for cast film, extrusion coating and lamination applications. The resin provides excellent film stiffness, temperature resistance and scratch resistance.

SCGC™ HDPE H455JA is a high density polyethylene resin with good processability, good mechanical and excellent organoleptic properties, designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H512W is a high density polyethylene for solid insulation in cable application. It is also suitable for outer skin in

SCGC™ HDPE H5211PC is a black, bimodal technology, high density polyethylene compound classified as MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. SCGC™ HDPE H5211PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H5480S is a high density polyethylene resin which is recommended for monofilament or flat yarn applications. It is specially designed for extrusion process both with spinneret die and T-die. H5480S offers good balance process ability and mechanical properties such as tenacity and elongation.

SCGC™ HDPE H555J is a high density polyethylene resin with good processability, mechanical and organoleptic properties. It is particularly designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H555JA is a high density polyethylene resin with good processability, mechanical and organoleptic properties. It is particularly designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H5604F is a high density polyethylene product of bi-modal process which suitable for the high quality film application. It is recommended for general purpose film with high tensile strength.

SCGC™ HDPE H567J is a high density polyethylene resin with good processing performance, excellent stress cracking resistance, designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H567JA is a high density polyethylene resin with good processing performance, excellent stress cracking resistance, designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H568JA is a high density polyethylene resin with excellent stress cracking resistance, designed for beverage
caps & closures with both injection molding and continuous compression molding.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

SCGC™ HDPE H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE

SCGC™ HDPE H624WC is a black bimodal high density polyethylene compound for jacketing of fiber optic and power cable applications. Its MFR and density are outer the traditional range which provide better processability, and also contains appropriate level of additives and well-dispersed carbon black to ensure excellent weathering resistance

SCGC™ HDPE H6308JU is a high density polyethylene resin with good processibility and UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE S414B is a high density polyethylene resin produced by SMX™ technology. This grade can be processed at high speed blow molding machine. It is recommended for milk bottles.

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ LLDPE L546WC is a black linear low density polyethylene compound for jacketing in communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0020P is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0040P is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0100F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0100P is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0200F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0400F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0500F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0600F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP0700F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1020P is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1022P is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1024P is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1040P is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1040T is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A refined polyethylene homopolymer wax, SCGC™ PE WAX LP1060P is produced using a distinctive high-density polyethylene (HDPE) technology that SCGC™ possesses in a closed-loop refinery. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP8110F is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

A polyethylene homopolymer wax, SCGC™ PE WAX LP8110P is produced using a distinctive high-density polyethylene (HDPE) technology. Our products are produced to precise quality control standards, with a narrow range of variability and consistent quality.

SCGC™ LLDPE M10 series are color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. These grades are suitable for rotational moulding of storage tanks and general purpose applications.

SCGC™ LLDPE M30 series are color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. These grades are suitable for containers and general applications which have wall thickness less than 5 mm. M30 Series designed for indoor and semi-indoor products with UV2.

SCGC™ M3204RU is a linear-low density polyethylene (LLDPE) for indoor/ semi-indoor rotational moulding applications. M3204RU is a natural color PE resin available in a pellet and powder form. This grade is suitable for containers and general purpose applications which are indoor/ semi-indoor or for thin wall parts. (Wall thickness less than 5 mm)

SCGC™ LLDPE M3504DXP is powder of a linear low density polyethylene octene copolymer for rotational molding applications. M3504DXP are specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks with a generous radius and curve.

SCGC™ M3565RW is a lilinear-low density polyethylene (LLDPE) with Hexene co-monomer (C6) for rotational moulding. M3565RW is a natural color PE resin aviailable in a pellet form.With a high UV resistance (8), good balancing of stiffness & impact, excellent surface finishing, good dimension tolerance and excellent ESCR, this grade suitable for rototional moulding of water tanks, chemical tanks and Automotive parts.

SCGC™ LLDPE M3804RU is a linear-low density polyethylene (LLDPE) for indoor / semi-indoor rotational moulding applications. M3804RU is a natural color PE resin available in a pellet and powder form. This grade is suitable for rotational moulding of storage tanks and general purpose applications which are indoor / semi-indoor or for thin wall (wall thickness less than 5 mm) parts.

SCGC™ LLDPE M3804RW and Marvel™ M10 are linear low density polyethylene (LLDPE) for rotational molding applications. M3804RW is a natural color PE resin available in a pellet and powder form, whereas M10 is the color compound version. These grades are suitable for rotational molding of storage tanks and general applications.

SCGC™ M3845RW is a lilinear-low density polyethylene (LLDPE) for rotational moulding. M3845RW is a natural color PE resin aviailable in a pellet form. With a high UV resistance (8), fast cooking, easy demolding, good dimension stability, this grade suitable for rotational moulding of water tanks

SCGC™ M3845RY is a lilinear-low density polyethylene (LLDPE) for rotational moulding. M3845RY is a natural color PE resin aviailable in a pellet form. With fast cooking, easy demolding, good dimension stability, this grade suitable for rotational moulding, this grade sustable for multi-purpose rotaional moulding applications

SCGC™ M3863RW is a lilinear-low density polyethylene (LLDPE) for rotational moulding with Hexene co-monomer (C6). M3863RW is a natural color PE resin aviailable in a pellet form. With an extra UV resistance (20), high stiffness and good impact resistance, long durability and excellent ESCR, this grade suitable for rotational moulding of large water tanks, undergroud tanks and chemical tanks

SCGC™ LLDPE M40 are color compound linear-low density polyethylene (LLDPE) for rotational molding applications. These grades are suitable for containers and general applications which have wall thickness less than 5 mm. M40 has UV8 protection for outdoor application.

SCGC™ LLDPE M50 series are color powder of a linear low density polyethylene octene copolymer for rotational molding applications. M50 series are specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks, fuel tank with a generous radius and curve.

SCGC™ MDPE M545WC is a black medium density polyethylene compound for jacketing in power cable and communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.

SCGC™ LLDPE M70 series are color powder of linear-low density polyethylene (LLDPE) for rotational moulding applications. M70 series are high melt flow and a balance of impact strength, stiffness, and processability, these grades are suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ LLDPE M72 is a color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. With a high melt flow and a balance of impact strength and processability, this grade is specifically designed for rotational moulding of cooler boxes, exhibiting an excellent surface finish with no pinholing.

SCGC™ M735RU is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RU is a natural color PE resin available in a pellet and powder form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of decorative items and small industrial parts.

SCGC™ M735RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RW is a natural color PE resin available in a pellet and powder form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ LLDPE M90 series are a linear-low density polyethylene (LLDPE) for rotational moulding applications. M90 series are the color compound version. This grade is suitable for rotational moulding of large water tanks and parts that require high stiffness.

SCGC™ LLDPE M9001RW is linear-low density polyethylene (LLDPE) for rotational molding applications. M9001RW is a natural color available in a pellet and powder form, These grades are suitable for rotational molding of large water tanks and parts that require high stiffness.

Our oxidized low-density polyethylene wax, OX102P, is manufactured using an unique manufacturing technique developed by SCGC™. Our products are meticulously made to guarantee a narrow range of variability in their properties and a constant level of product quality. SCGC™'s Oxidized low-density polyethylene wax is specifically made for PVC, textile, and paint and coating applications.

SCGC™ PP P1085J is high crystalline polypropylene impact copolymer. It is designed for compounding base. This resin is recommended for automotive and appliance compounding products that require high melt flow rate for thin wall parts.

SCGC™ PP P303S is a homopolymer polypropylene resin with high stiffness and high clarity. It is designed for sheet and solid phase pressure thermoforming products.

SCGC™ PP P348S is a special impact copolymer polypropylene base resin with high thermal stability and high impact strength at low temperature. It is designed for sheet and solid phase pressure thermoforming.

SCGC™ PP P350F is a copolymer polypropylene without slip and anti-blocking agents for cast film application with excellent seal properties, excellent clarity and good stress whitening resistance.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCGC™ PP P443J is an impact copolymer polypropylene resin with good processability and good mechanical properties, designed for beverage caps & closures with both injection molding and continuous compression molding.

SCGC™ PP P601F is a homopolymer polypropylene resin for water-quenched blown film.This grade is contain high slip and antiblock agent and recommended for applications that film thickness is lower than 50 micron.

SCGC™ PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. This grade is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

SCGC™ PP P607F is a homopolymer polypropylene resin without slip and antiblock agents for a core layer of co-extrusion cast film or monolayer cast film applications. It offers high film stiffness, good clarity and processability.

SCGC™ PP P639AT is very high flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is suggested for compounds that require low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P655IM is the polypropylene random copolymer resin that is well-suited to healthcare and pharmaceutical products with good clarity. P655IM is designed for product produced by Injection Stretch Blow Molding (ISBM) process. P655IM is compliant to FDA, USP, and EP requirements.Notice : It is strongly recommended that all potential activities for applications related to pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with SCGC™

SCGC™ PP P704JM is a homopolymer polypropylene resin that is well-suited to healthcare and pharmaceutical products. P704JM has good processability, high clarity and is compliant to FDA and USP requirements.P704JM can be injection molded and sterilized by ethylene oxide.

SCGC™ PP P705JM is homopolymer polypropylene resin that is well-suited to healthcare and pharmaceutical products. P705JM has good processability, high stiffness and is compliant to FDA, USP, and EP requirements.P705JM can be injection molded and sterilized by ethylene oxide.Notice : It is strongly recommended that all potential activities for applications related to pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with SCGC™

SCGC™ PP P739ET is high flowability polypropylene impact copolymer. It is designed for compounding base and injection molding process. This resin is recommended for compounds that require good surface aesthetics and low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P747WT is low gloss and medium flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is recommended for product which require good surface aesthetics and stiffness/impact balance. It is suitable for various automotive parts.

SCGC™ PP P765J is very high impact polypropylene copolymer. It is designed for automotive interior and exterior parts such as door trims, instrumental panel and bumper which it’s suitable for injection molding process. This resin is recommended for product that require very high impact strength at room temperature and low temperature.

SCGC™ PP P809JM is a homopolymer polypropylene resin that is well-suited to healthcare and pharmaceutical products. P809JM has good processability, high clarity and is compliant to FDA and USP requirements.P809JM can be injection molded and sterilized by ethylene oxide.Notice : It is strongly recommended that all potential activities for applications related to pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with SCGC™

SCGC™ PP P838C is a polypropylene product which is specially designed for extrusion coating or lamination coating with PP substrate application. P838C can be used in several coating application for example coated woven bag, tarpaulin, laminated with PP substrate which is required stiffness of finish products.

SCGC™ P901J is polypropylene homopolymer with excellent flowability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding.

SCGC™ PVC PC750 is a high molecular weight homoploymer paste PVC resin, produced by TPC Paste Co.,Ltd. under OxyChem's HYBRID technology

PF621 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

PF682 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

SCGC™ PVC PF741 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG680 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG740 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG770 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ HDPE S1000P is a natural, tri-modal, high density polyethylene resin designed as a general base resin of color compound for pipe extrusion and stripe.

S111F is a high strength polyethylene produced by SMX™ technology which superior toughness and stiffness. This grade can be processed at high output blown film extrusion with excellent bubble stability. It is recommended for high quality film application such as industrial bag and products for property modification

SCGC™ LLDPE S15 is a special linear-low density polyethylene (LLDPE) designed for strong adhesion to polyurethane foam (PU foam). S15 helps eliminate internal surface modification step since PU foam can be applied directly right after molding and reduce reject rates due to improper internal surface modification, in addition to reducing additional raw material procurement and increasing safety in the work station. It is suitable for temperature insulated applications.

SCGC™ HDPE S16 is a color compound high-density polyethylene (HDPE) for rotational moulding applications. S16 is designed for parts that require excellent stiffness and impact strength. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and durability.

S199F is a high strength polyethylene produced by SMX™ technology, resulting in better impact strength with excellent process ability. This grade can be produced various film widths from wider operating condition with balancing between mechanical properties and bubble stability. It is recommended for high quality film application in consumer and industrial segment such as general purpose film.

SCGC™ S411B is a high strength polyethylene resin designed for small blow (upto 6L) molding containers. This grade provides excellent combination of stiffness and chemical resistance for container light weighting.

SCGC™ S495B is a high strength polyethylene resin designed to provides excellent combination of stiffness and chemical resistance for blow molding container size upto 30L

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl chloride homopolymer having low molecular weight with high porosity. SF58S is white and free-flowing resins produced by suspension polymerization process. The resin is recommended to use for chlorinated poly vinyl chloride process to produce chlorinated poly vinyl chloride (CPVC). Applications are ranging from general purpose to special products regarding customer’s satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. The medical grade PVC resin is developed for medicals application which more concerned about health safety.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC GREEN POLYMER™ SX002J is a high density polyethylene resin with superior stress cracking resistant and excellent mechanical property balance. It is particularly designed for light-weight carbornated soft drink caps. This resin has excellent processability for both injection molding and continuous compression molding.

SCGC GREEN POLYMER™ SX002JA is a high density polyethylene resin with superior stress cracking resistant and excellent mechanical property balance. It is particularly designed for light-weight carbornated soft drink caps. This resin has excellent processability for both injection molding and continuous compression molding.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2020P is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2020PX is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2040P is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2040PX is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2110P is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

The distinguished class of polyethylene homopolymer wax with distinctive qualities known as WD2110PX is created by the thermal cracking technology. Notwithstanding the SCGC™'s experience and cutting-edge technology, wax has a uniform color and physical properties that enable it to be utilized in a variety of applications.

SCGC™ PP X811T is high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

SCGC™ PP X861T is a high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

60701WHA is a thermoplastic polyolefin (TPO) compound. The product is designed for extrusion process in application of soft profile, gasket, seal, and etc.

PCRH01BN is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM grade PCRH02BW is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM grade PCRH03BB is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM PCRP01JN is a certified Post-Consumer Recycled Resin polypropylene. This grade is suitable for injection molding application using injection molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM grade PCDH01BN is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM grade PCDH02BW is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM PCDP01JN is a certified Post-Consumer Recycled Resin polypropylene with odorless feature. This grade is suitable for injection molding application using injection molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMERTM grade BIOC01FN is a Bio-Compostable Compound Resin designed for film products which require excellent stiffness, ease processing properties and less odor. It is particularly designed for blown film extrusion. This grade is suitable for compostable film products.

SCGC Green PolymerTM grade AP303S is a circular polypropylene homopolymer resin, the development of advanced recycling technology that turn post consumer plastic into renewable feedstock for virgin plastic resin plastic resin production

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ HDPE H1000PCH is a black, bimodal technology, high density polyethylene compound. It is classified as a PE100RC material with excellent resistance to crack, following the material requirements of EN1555-1:2021.

SCGC™ GREEN POLYMER S197F

SCGC™ GREEN POLYMER P408F is homo polypropylene resin for biaxially oriented polypropylene film. This resin is designed for superior heat resistance and higher stiffness which is suitable for full PP packaging.

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in op

Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result

Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.

SCGC PP P905J is a homopolymer polypropylene resin with high flowability, ultra clarity and good mechanical property balance. It is particularly designed for the injection moulding of transparent packaging.

SCGC SOLUTIONS

Irrigation System