Description

SCGC™ HDPE H1000PC is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

Properties Test Methods Value Unit
Melt Flow Rate at 190 °C and 5.0 kg ISO 1133 0.24 g/10 min
Density ISO 1183 0.960 g/cm³
Tensile Strength at Yield (100 mm/min) ISO 527 24 MPa
Tensile Strength at Break (100 mm/min) ISO 527 > 30 MPa
Elongation at Break (100 mm/min) ISO 527 > 600 %
Carbon black dispersion (Grading) ISO 18553 ≤ 3 -
Carbon black content ISO 6964 2.25 %wt
Oxidative induction time at 210°C ISO 11357 ≥ 40 min
Flexural Modulus ASTM D 790 1,000 MPa
MRS classification ISO 12162/ISO 9080 10 MPa
Resistance to slow crack growth at 80°C ISO 13479 ≥ 500 hrs
Rapid crack propagation Pc, S4 ISO 13477 ≥ 10 bar
Resistance to gas constituents ISO 1167 ≥ 20 hrs
DOWNLOADS
Data Sheet
Safety Data Sheet
Brochure

RELATED PRODUCT GRADES

SP661
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
D682PC
SCGC™ LLDPE D682PC is a black linear low density polyethylene compound. Well dispersed carbon black creates outstanding UV resistance and thermal stability.
H1000PBL
SCGC™ HDPE H1000PBL is a blue (no lighter than RAL 5005), trimodal, high density polyethylene compound that is specially designed for water pressure pipes, especially for drinking water pipes. SCGC™ HDPE H1000PBL is designed as PE100 pipes providing excellent in mechanical properties, and processability. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term using.
H1000PCI
SCGC™ HDPE H1000PCI is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. It is particularly designed for injection molding for pipe fittings.In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
H1000PWI
SCGC™ HDPE H1000PWI is a white HDPE compound made for external layer of above ground pipe applications. It provides high mechanical properties, good processability, and low heat absorption. In addition the good dispersion and high concentration of stabilizers contribute excellent long term UV resistance and thermal stability.
H112PC
SCGC™ HDPE H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology. SCGC™ HDPE H112PC is classified as MRS 11.2 material (PE112). It provides superior long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides that, it can be produced in all ranges of pipe diameters, especially recommended for the production of very thick wall and large diameter pipe.
S1000P
SCGC™ HDPE S1000P is a natural, tri-modal, high density polyethylene resin designed as a general base resin of color compound for pipe extrusion and stripe.
SF580
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction
SF581
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions
SG500
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SG580
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SG58J
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SG610
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SG61J
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SP660
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
SP66J
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
H1000PCH
SCGC™ HDPE H1000PCH is a black, bimodal technology, high density polyethylene compound. It is classified as a PE100RC material with excellent resistance to crack, following the material requirements of EN1555-1, EN12201-1, ISO4437-1.
S999PC
SCGC™ HDPE S999PC Very High Abrasion Resistance (VHAR) is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, tri-modal technology. It provides superior abrasion resistance which is especially recommended for aggressive slurry media transferring Mining and Dredging application. It has been designed for good long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance together with excellent sagging resistance property.
arrow-02-r
arrow-02-l

Market & Application

Agriculture & Horticulture
Agriculture & Horticulture
Infrastructure
Infrastructure
icon-arrow-right
icon-arrow-left
dot footer
SCG Chemicals
Public Company Limited
1 Siam Cement Road, Bangsue,
Bangkok 10800 Thailand
icon-phone+662-586-1111
arrow-right-1Contact Us icon searchSubscribe
Follow us :
  • icon-fb
  • icon-tw
  • icon-yt
  • icon-in
  • icon-line

Copyright © SCG Chemicals Public Company Limited (2022). All Rights Reserved.