S1000P

SCGC™ HDPE S1000P is a natural, tri-modal, high density polyethylene resin designed as a general base resin of color compound for pipe extrusion and stripe.

Properties	Test Methods	Value	Unit
Melt Flow Rate at 190 °C and 5.0 kg	ASTM D 1238	0.19	g/10 min
Melt Flow Rate at 190 °C and 21.6 kg	ASTM D 1238	6.25	g/10 min
Density	ASTM D 1505	0.949	g/cm³
Tensile Strength at Yield	ISO 527	23	MPa
Tensile strength at Break	ISO 527	40	MPa
Elongation at Break	ISO 527	750	%
Oxidative induction time at 200°C	ISO 11357	> 40	min
ESCR 10% Igepal, F0	ASTM D 1693	> 10,000	hrs

RELATED PRODUCT GRADES

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC™ LLDPE D682PC is a black linear low density polyethylene compound. Well dispersed carbon black creates outstanding UV resistance and thermal stability.

SCGC™ HDPE H1000PBL is a blue (no lighter than RAL 5005), trimodal, high density polyethylene compound that is specially designed for water pressure pipes, especially for drinking water pipes. SCGC™ HDPE H1000PBL is designed as PE100 pipes providing excellent in mechanical properties, and processability. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term using.

SCGC™ HDPE H1000PC is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PCI is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. It is particularly designed for injection molding for pipe fittings.In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PWI is a white HDPE compound made for external layer of above ground pipe applications. It provides high mechanical properties, good processability, and low heat absorption. In addition the good dispersion and high concentration of stabilizers contribute excellent long term UV resistance and thermal stability.

SCGC™ HDPE H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology. SCGC™ HDPE H112PC is classified as MRS 11.2 material (PE112). It provides superior long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides that, it can be produced in all ranges of pipe diameters, especially recommended for the production of very thick wall and large diameter pipe.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

SCGC™ HDPE H1000PCH is a black, bimodal technology, high density polyethylene compound. It is classified as a PE100RC material with excellent resistance to crack, following the material requirements of EN1555-1, EN12201-1, ISO4437-1.

SCGC™ HDPE S999PC Very High Abrasion Resistance (VHAR) is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, tri-modal technology. It provides superior abrasion resistance which is especially recommended for aggressive slurry media transferring Mining and Dredging application. It has been designed for good long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance together with excellent sagging resistance property.

Market & Application

Agriculture & Horticulture

Agriculture & Horticulture