EL-Pro™ P303S is a homopolymer polypropylene resin which is suitable for sheet and thermoforming products that required high stiffness and high clarity. It is particularly designed for solid phase pressure forming.
Related Finished Products
Dairy cups, disposable drinking cups, food containers for microwave heating
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.91
Elongation at break (%)
ASTM D 638 @ Crosshead speed 50 mm/min
7
Flexural Modulus (kg/cm2)
ASTM D 790
19000
Haze at 1 mm thickness
(%)
ASTM D 1003
23
HDT
(°C)
ASTM D 648
128
IZOD 23 °C (kg.cm/cm)
ASTM D 256
6
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
2
Tensile Strength at Yield(kg/cm2)
ASTM D 638 @ Crosshead speed 50 mm/min
400
P400S
13500
4
3.5
Description
EL-Pro™ P400S is a homopolymer polypropylene resin which provides high productivity with balance machanical properties, and food contact application.
Related Finished Products
Woven sack, strap, tarpauline straw, and sheet.
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.91
Flexural Modulus
(Mpa)
ASTM D 790
16000
Flexural Modulus (kg/cm2)
ASTM D 790
13500
IZOD 23 °C (kg.cm/cm)
ASTM D 256
4
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
3.5
P401S
14250
4.2
2.4
Description
EL-Pro™ P401S is a homopolymer polypropylene resin which provides high strength of flat yarn, good thermal stability and food contact application.
Related Finished Products
Woven bag, tarpauline, rope, sheet and thermoform.
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.91
Flexural Modulus
(Mpa)
ASTM D 790
16000
Flexural Modulus (kg/cm2)
ASTM D 790
14250
IZOD 23 °C (kg.cm/cm)
ASTM D 256
4.2
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
2.4
P403J
3.5
Description
EL-Pro™ P403J is a polypropylene resin which provides good impact resistance and high gloss with ordorless. Food contact is also applicable.
Related Finished Products
Furniture, fruit basket, household products, toys, office accessories, food container, cap & closure, and infant articles
Properties
Test Methods
Value
Flexural Modulus
(Mpa)
ASTM D 790
13500
Flexural Modulus (kg/cm2)
ASTM D 790
IZOD
-
4
IZOD 23 °C (kg.cm/cm)
ASTM D 256
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
3.5
P500J
15500
3.5
8
-
Description
EL-Pro™ P500J is a homopolymer polypropylene resin suitable for compounding and injection moulding. It provides excellent stiffness, high gloss, thermal stability and processibility.
Related Finished Products
Electrical appliance compounding mainly for refrigerator parts, and washing machine parts such as compound outer tub
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.9
Flexural Modulus (kg/cm2)
ASTM D 790
15500
HDT at 0.45 Mpa (°C)
ASTM D 648
100
Izod -20 °C (kg.cm/cm)
ASTM D 256
2
IZOD 0 °C (kg.cm/cm)
ASTM D 256
2
IZOD 23 °C (kg.cm/cm)
ASTM D 256
3.5
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
8
P600F
17000
-
10
Description
EL-Pro™ P600F is a homopolymer polypropylene resin which provides good optical properties and good openability.
Related Finished Products
Water-quenched blown film for food and clothes packaging
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.91
Flexural Modulus (kg/cm2)
ASTM D 790
17000
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
10
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 280, TD 260
P600FS
14500
-
12
-
Description
EL-Pro™ P600FS is a homopolymer polypropylene resin which provides excellent openability and excellent optical.
Related Finished Products
Water-quenched blown film for thin packaging (<20 micron)
Properties
Test Methods
Value
Elongation at break (%)
ASTM D 638 @ Crosshead speed 50 mm/min
MD 450, TD 30
Flexural Modulus (kg/cm2)
ASTM D 790
14500
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
12
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 220, TD 80
P602F
17000
-
10
Description
EL-Pro™ P602F is a homopolymer polypropylene resin which provides excellent optical properties and high productivity.
Related Finished Products
Water-quenched blown film for thick packaging
Properties
Test Methods
Value
Flexural Modulus (kg/cm2)
ASTM D 790
17000
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
10
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 280, TD 260
P607F
7
Description
EL-Pro™ P607F is a homopolymer polypropylene resin without slip and antiblocking agent suitable for cast film application as a core layer of a co-extrusion film or a monolayer film requiring high film stiffness and high clarity.
Related Finished Products
Monolayer cast film, core layer for co-extrusion cast film, metallized film
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.91
Flexural Modulus
(Mpa)
ASTM D 790
1607
Flexural Modulus (kg/cm2)
ASTM D 790
Gloss
(%)
ASTM D 2457
84
Haze
(%)
ASTM D 1003
1.3
IZOD 23 °C (kg.cm/cm)
ASTM D 256
Melt flow rate at 230 °C, 2.16 kg. (g/10 min)
ASTM D 1238
7
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
7
Tensile Modulus, 2% Secant(kg/cm2)
ASTM D 882
MD5200, TD3900
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 370, TD 90
Tensile Strength at Yield(kg/cm2)
ASTM D 638 @ Crosshead speed 50 mm/min
MD 290, TD 230
Thickness
(micron)
-
20
VICAT Softening Temperature
(°C)
ASTM D 1525
154
P700J
14500
3
12
Description
EL-Pro™ P700J is a homopolymer polypropylene resin, suitable for compounding and injection moulding. It provides high stiffness, gloss, thermal stability and processibility. Also, food contact is applicable.
Related Finished Products
Electrical appliance compounding mainly for washing machine parts (such as compound outer tub), furniture, fruit basket, household products, toys, office accessories, food container, infant articles
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.9
Flexural Modulus (kg/cm2)
ASTM D 790
14500
IZOD 23 °C (kg.cm/cm)
ASTM D 256
3
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
12
P701J
-
-
12
Description
EL-Pro™ P701J is a homopolymer polypropylene resin which provides high processability, ordorless, and good stiffness. Also, food contact is applicable.
EL-Pro™ P702J is a homopolymer polypropylene resin which provides high clarity and gloss, high stiffness, high processability, ordorless, and gloss. Also, Food contact is applicable.
Related Finished Products
Household products, toys, and containers
Properties
Test Methods
Value
Flexural Modulus
(Mpa)
ASTM D 790
17000
IZOD
-
3.5
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
12
P704JM
15000
34
-
Description
EL-Pro P704JM is a homopolymer polypropylene resin that is well-suited to healthcare and pharmaceutical products. P704JM has good processability, high clarity and is compliant to FDA and USP requirements.P704JM can be injection molded and sterilized by ethylene oxide.
Related Finished Products
Properties
Test Methods
Value
Flexural Modulus (kg/cm2)
ASTM D 790
15000
IZOD 23 °C (kg.cm/cm)
ASTM D 256
34
Melt flow rate at 230 °C, 2.16 kg. (g/10 min)
ASTM D 1238
12
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
P705JM
14500
3
12
Description
EL-Pro™ P705JM is a homopolymer polypropylene resin that is well-suited to healthcare and phamaceutical products, P705JM has good processability, high stiffness and is compliant to FDA and USP requirements.
Related Finished Products
Ethylene Oxide (EO) sterilization for Medical Plastic Resins Devices & Diagnostic Lab Wares
Properties
Test Methods
Value
EP 3.1.6
-
Complied
Flexural Modulus (kg/cm2)
ASTM D 790
14500
IZOD 23 °C (kg.cm/cm)
ASTM D 256
3
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
12
US FDA 21 CFR 177.1520
-
Complied
USP Class 6
-
Complied
P901J
16500
3
60
Description
EL-Pro™ P901J is a homopolymer polypropylene resin with excellent flowability, high stiffness and high clarity. This grade is suitable for thin wall injection molding for food, beverage and general packaging.
Related Finished Products
Thin wall food and beverage packaging;
- Food containers with high stiffness
- Drinking cups with high clarity
General thin wall products
Housewares
Properties
Test Methods
Value
% Shrinkage (MD/TD)
TPE Method
1.2/1.4
Density (g/cm3)
ASTM D 1505
0.91
Flexural Modulus (kg/cm2)
ASTM D 790
16500
Haze at 1 mm thickness
(%)
ASTM D 1003
35
HDT
(°C)
ASTM D 648
125
IZOD 23 °C (kg.cm/cm)
ASTM D 256
3
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
60
P902J
16500
4
60
-
Description
EL-Pro P902J is a homopolymer polypropylene resin with excellent flow ability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding for food, beverage and general packaging
Related Finished Products
Thin wall food and beverage packaging; Food containers, Drinking cups, General thin wall products, Housewares
Plastic containers have enjoyed continuing popularity due to the way they fit the modern lifestyle which values both convenience and speed. In Thailand, the packaging industry grows by approximately 3 - 4 per cent annually. However, growing environmental concernamong consumers has led them to choose products which are friendly to the environment. Packaging manufacturers therefore have started to put more emphasis on the development of environmentally-friendly products. One way to do this has been the use of raw materials that produce thinner and lighter packaging while maintaining other properties that give the consumers the convenience and ease of use that they need.
As part of its attempt to develop environmentally-friendly innovations, SCG Chemicals has researched and developed an innovative new plastic resin, P902J, which responds to the needs of both manufacturers of thin wall injection molding food and drink packaging as well as consumers. With its product development team who are skilled in the development of plastic packaging materials and its state-of-the-art laboratory, SCG Chemicals has been able to develop these environmentally friendly plastic resins with possess properties that make them stand out from ordinary plastic resins for injection.
Highlights of P902J include:
Being thinner yet stronger:
P902J helps reduce the amount of plastic resins used in the production process causes cost saving. From 40 - 60 % higher toughness than conventional PP resin for injection, it is stronger and does not become brittle and break easily while in use of thinner and lighter product. With greater isotropic shrinkage, the packaging does not bend out of shape which makes it easier for consumers to use. Moreover, its high transparency gives it an attractive look. The fact that it is thinner and lighter also means a higher volume of goods can be transported at one time.
Increased productivity:
Its high flowability and faster demolding contribute directly to the manufacturing process, as it helps manufacturers to produce more products in the same amount of time with the molding time being cut by 5 - 10 per cent.
Reduced energy consumption in the manufacturing process:
The high flowability and faster demolding means the need for energy in the range ofprocesses involved from resin production to packaging manufacturing can be reduced. It is easier to produce thinner packaging as the resin can fast flowing by using less energy to melt. Moreover, the ability to be fast solidified also savethe energy to cool the product. It is an opportunity to do 5 times faster cooling in same product size.
This is just one example of how it is possible and worthwhile to conserve the environment through research and development of P902J plastic resins, and that these resins are a good alternative for plastic packaging manufacturers who are looking for environmentally-friendly innovations which can effectively serve the needs of consumers.
For more information aboutP902Jplease visithttps://www.scgchemicals.com/en/products-services/product-type/pp/pp-homopolymer
PP Homopolymer
Total 16 grades
EL-Pro™ PP homopolymer is a polypropylene resin produced with a technology developed by Mitsui Chemical Inc. of Japan.
EL-Pro™ P303S is a homopolymer polypropylene resin which is suitable for sheet and thermoforming products that required high stiffness and high clarity. It is particularly designed for solid phase pressure forming.
Related Finished Products
Dairy cups, disposable drinking cups, food containers for microwave heating
EL-Pro™ P500J is a homopolymer polypropylene resin suitable for compounding and injection moulding. It provides excellent stiffness, high gloss, thermal stability and processibility.
Related Finished Products
Electrical appliance compounding mainly for refrigerator parts, and washing machine parts such as compound outer tub
EL-Pro™ P607F is a homopolymer polypropylene resin without slip and antiblocking agent suitable for cast film application as a core layer of a co-extrusion film or a monolayer film requiring high film stiffness and high clarity.
Related Finished Products
Monolayer cast film, core layer for co-extrusion cast film, metallized film
EL-Pro™ P700J is a homopolymer polypropylene resin, suitable for compounding and injection moulding. It provides high stiffness, gloss, thermal stability and processibility. Also, food contact is applicable.
Related Finished Products
Electrical appliance compounding mainly for washing machine parts (such as compound outer tub), furniture, fruit basket, household products, toys, office accessories, food container, infant articles
EL-Pro™ P701J is a homopolymer polypropylene resin which provides high processability, ordorless, and good stiffness. Also, food contact is applicable.
EL-Pro™ P702J is a homopolymer polypropylene resin which provides high clarity and gloss, high stiffness, high processability, ordorless, and gloss. Also, Food contact is applicable.
EL-Pro P704JM is a homopolymer polypropylene resin that is well-suited to healthcare and pharmaceutical products. P704JM has good processability, high clarity and is compliant to FDA and USP requirements.P704JM can be injection molded and sterilized by ethylene oxide.
EL-Pro™ P705JM is a homopolymer polypropylene resin that is well-suited to healthcare and phamaceutical products, P705JM has good processability, high stiffness and is compliant to FDA and USP requirements.
Related Finished Products
Ethylene Oxide (EO) sterilization for Medical Plastic Resins Devices & Diagnostic Lab Wares
EL-Pro™ P901J is a homopolymer polypropylene resin with excellent flowability, high stiffness and high clarity. This grade is suitable for thin wall injection molding for food, beverage and general packaging.
Related Finished Products
Thin wall food and beverage packaging;
- Food containers with high stiffness
- Drinking cups with high clarity
General thin wall products
Housewares
EL-Pro P902J is a homopolymer polypropylene resin with excellent flow ability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding for food, beverage and general packaging
Related Finished Products
Thin wall food and beverage packaging; Food containers, Drinking cups, General thin wall products, Housewares
Plastic containers have enjoyed continuing popularity due to the way they fit the modern lifestyle which values both convenience and speed. In Thailand, the packaging industry grows by approximately 3 - 4 per cent annually. However, growing environmental concernamong consumers has led them to choose products which are friendly to the environment. Packaging manufacturers therefore have started to put more emphasis on the development of environmentally-friendly products. One way to do this has been the use of raw materials that produce thinner and lighter packaging while maintaining other properties that give the consumers the convenience and ease of use that they need.
As part of its attempt to develop environmentally-friendly innovations, SCG Chemicals has researched and developed an innovative new plastic resin, P902J, which responds to the needs of both manufacturers of thin wall injection molding food and drink packaging as well as consumers. With its product development team who are skilled in the development of plastic packaging materials and its state-of-the-art laboratory, SCG Chemicals has been able to develop these environmentally friendly plastic resins with possess properties that make them stand out from ordinary plastic resins for injection.
Highlights of P902J include:
Being thinner yet stronger:
P902J helps reduce the amount of plastic resins used in the production process causes cost saving. From 40 - 60 % higher toughness than conventional PP resin for injection, it is stronger and does not become brittle and break easily while in use of thinner and lighter product. With greater isotropic shrinkage, the packaging does not bend out of shape which makes it easier for consumers to use. Moreover, its high transparency gives it an attractive look. The fact that it is thinner and lighter also means a higher volume of goods can be transported at one time.
Increased productivity:
Its high flowability and faster demolding contribute directly to the manufacturing process, as it helps manufacturers to produce more products in the same amount of time with the molding time being cut by 5 - 10 per cent.
Reduced energy consumption in the manufacturing process:
The high flowability and faster demolding means the need for energy in the range ofprocesses involved from resin production to packaging manufacturing can be reduced. It is easier to produce thinner packaging as the resin can fast flowing by using less energy to melt. Moreover, the ability to be fast solidified also savethe energy to cool the product. It is an opportunity to do 5 times faster cooling in same product size.
This is just one example of how it is possible and worthwhile to conserve the environment through research and development of P902J plastic resins, and that these resins are a good alternative for plastic packaging manufacturers who are looking for environmentally-friendly innovations which can effectively serve the needs of consumers.
For more information aboutP902Jplease visithttps://www.scgchemicals.com/en/products-services/product-type/pp/pp-homopolymer