EL-Lene™ F15 is a high density polyethylene resin which provides high tensile strength and high productivity.
Related Finished Products
Film produced by high speed machine and wide lay flat (>25")
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.952
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.06
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 910, TD 380
H1000PBL
-
-
-
Description
EL-Lene™ H1000PBL is a blue (no lighter than RAL 5005), bimodal, high density polyethylene compound that is specially designed for water pressure pipes, especially for drinking water pipes. It is designed as PE100 pipes providing excellent in mechanical properties and processablitiy. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term use.
Related Finished Products
Drinking water pipe and stripe lines for PE100
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.951
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.27
H1000PC
-
-
-
Description
EL-Lene™ H1000PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.25
H1000PCI
-
-
-
Description
EL-Lene™ H1000PCI is a black, bimodal technology, high density polyethylene compound designed for injection molding fitting. It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Related Finished Products
Injection grade for butt-fusion and electrofusion fittings
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.96
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.4
H1000PWI
-
-
-
Description
EL-Lene™ H1000PWI is a white HDPE compound using bimodal technology to provide superior mechanical properties, processablity, and low heat absorption. In addition, it has UV stabilizer and anti-oxidant package which combined with good dispersion of the white pigment results in excellent long term UV resistance and thermal stability.
Related Finished Products
Low heat absorption grade. Exernal coating for above ground pipe
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.972
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.25
H103S
0.962
18
-
-
Description
EL-Lene™ H103S is a high density polyethylene resin which provides very low gel, softness and anti gas-fading.
Related Finished Products
Hygiene products such as baby diapers, sanitary napkins and softness non-woven
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.962
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
18
H112PC
-
-
-
Description
EL-Lene™ H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology.It is classified as a MRS 11.2 material (PE112) which provides superior long - term hydro static strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides, it can be produced in all range of pipe diameters, recommended for the production of very thick wall and large diameter pipe.
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.2
H2001WC
0.963
0.13
-
Description
EL-Lene™ H2001WC is a black bimodal high density polyethylene compound for jacketing in fiber optic and power cable applications. It contains well-dispersed carbon black of nominal particle size less than 20 nanometer to provide excellent weathering resistance and UV resistance.
Related Finished Products
Jacketing of fiber optic cables, Jacketing of power cables
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.963
Elongation at break (%)
ASTM D 638 @ Crosshead speed 50 mm/min
840
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.13
Tensile at break (Mpa)
ASTM D 638 @ Crosshead speed 50 mm/min
34
H355JA
0.961
7.5
-
Description
EL-Lene™ H355JA is a high density polyethylene resin with good processability, mechanical property, and excellent organoleptic property. It is particularly designed for injection molding and continuous compression molding of caps and closures for the beverage packaging, especially for lightweight cap design.
Related Finished Products
Caps and closures for still and mineral water, juice, tea, and hot-filled beverages
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.961
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
7.5
H377C
0.961
7.5
-
Description
EL-Lene™ H377C is a bi-modal high density polyethylene resin for film casting and extrusion.
Related Finished Products
Extrusion coating, lamination or casting for various packaging (for blending with LDPE and LLDPE)
Properties
Test Methods
Value
Brittleness Temperature
(°C)
ASTM D 746
Dart Impact Strength
(g)
-
<60
Density (g/cm3)
ASTM D 1505
0.961
Elemendoft Tear Strength
(g)
ASTM D 1922
MD 24, TD 27
Gloss
(%)
ASTM D 2457
79
Haze
(%)
ASTM D 1003
9
Melt flow rate at 190 °C, 2.16 kg. (g/10 min)
ASTM D 1238
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
7.5
Tensile Modulus, 2% Secant(kg/cm2)
ASTM D 882
MD3981, TD4769
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 245, TD 290
Tensile Strength at Yield(kg/cm2)
ASTM D 638 @ Crosshead speed 50 mm/min
MD 234, TD 255
Thickness
(micron)
-
30
VICAT Softening Temperature
(°C)
ASTM D 1525
127
H455JA
0.958
4.5
-
Description
EL-Lene™ H455JA is a high density polyethylene resin with good processability, mechanical property, and excellent organoleptic property. It is particularly designed for injection molding and continuous compression molding of caps and closures for the beverage packaging.
Related Finished Products
Caps and closures for still and mineral water, juice, and tea
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.958
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
4.5
H511W
0.949
0.9
-
Description
EL-Lene™ H511W is a high density polyethylene resin for solid insulation in cable application. It is also suitable for outer skin in "foam-skin" constructions. It provides good performance across the full range of tele-communication insulation applications, including aircore and petroleum jelly filled cable designs in both buried and aerial environments.
Related Finished Products
Insulation of communication cables
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.949
Elongation at break (%)
ASTM D 638 @ Crosshead speed 50 mm/min
600
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.9
Tensile at break (Mpa)
ASTM D 638 @ Crosshead speed 50 mm/min
34
H5211PC
-
-
-
Description
EL-Lene™ H5211PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Related Finished Products
Drinking water, gas, conduit, corrugated pipes
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.96
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
ASTM D1238
0.4
H5480S
0.952
0.8
-
Description
EL-Lene™ H5480S is a high density polyethylene resin which provides high tenacity, good weathering, and easy processing.
Related Finished Products
Net & ropes, sun shading, tarpulin, and woven bag
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.952
Flexural Modulus (kg/cm2)
ASTM D 790
10000
IZOD 23 °C (kg.cm/cm)
ASTM D 256
17
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.8
H555J
0.953
1.8
-
Description
EL-Lene™ H555J is a high density polyethylene resin with good environmental stress cracking resistance, good processing performance, and organoleptic property. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures. Also, slip agent is contained to ensure easy-to-open.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.953
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
1.8
H555JA
0.953
1.8
-
Description
EL-Lene™ H555JA is a high density polyethylene resin with good environmental stress cracking resistance, good processing performance, organoleptic property. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
Related Finished Products
Caps and closures for carbonated soft drinks, hot fill beverages and water
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.953
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
1.8
H5604F
0.954
0.04
-
Description
EL-Lene™ H5604F is a high density polyethylene resin which provides high tensile strength.
Related Finished Products
General film
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.954
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.04
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 620, TD 310
H567J
0.952
1
-
Description
EL-Lene™ H567J is a high density polyethylene resin with excellent processing performance and mechanical properties, especially for environmental stress cracking resistance. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures. It also contains slip agent ensuring easy opening.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.952
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
1
H567JA
0.952
1
-
Description
EL-Lene™ H567JA is a high density polyethylene resin with excellent processing performance and mechanical properties, especially for environmental stress cracking resistance. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.952
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
1
H568JA
0.956
0.8
-
-
-
Description
H568JA is high density polyethylene resin with excellent environmental stress cracking resistance and good mechanical property
balance. It is particularly designed for light-weight carbonated soft drink caps. This resin have excellent processability for both
injection molding and continuous compression molding.
Related Finished Products
Beverage caps and closures : Carbonated soft drink, Sparkling water
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.956
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.8
H5814J
0.958
-
-
-
Description
EL-LeneTM H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process, this good flow ability grade designed for high productivity with good toughness product.
Related Finished Products
General injection parts
Household product
Bottle cap and closure
Toy
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.958
Flexural Modulus (kg/cm2)
ASTM D 790
12,500
Melt flow rate at 190 °C, 2.16 kg. (g/10 min)
ASTM D 1238
14
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
H5840B
0.955
0.4
-
Description
EL-Lene™ H5840B is a high density polyethylene resin which provides excellent ESCR, good surface appearance, good processability and good printability.
Related Finished Products
Chemical bottles, personal and homecare bottles, lube oil bottles
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.955
Flexural Modulus
(Mpa)
ASTM D 790
12000
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.4
H6140B
0.960
0.3
-
Description
EL-Lene™ H6140B is a high density polyethylene resin which provides excellent surface appearance, good impact strength, processability and printability.
Related Finished Products
Personal and homecare bottles, lube oil bottles.
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.960
Flexural Modulus
(Mpa)
ASTM D 790
13000
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.3
H619F
0.965
0.7
-
Description
EL-LeneTM H619F is a high stiff homopolymer HDPE designed to improve film stiffness and barrier properties when co-extruded with LLDPE & LDPE. It also provides good film clarity and processability when used in the core layer with an excellent compatibility with LLDPE & LDPE.
Properties
Test Methods
Value
Dart Impact Strength
(g)
-
<32
Density (g/cm3)
ASTM D 1505
0.965
Elemendoft Tear Strength
(g)
ASTM D 1922
MD 7, TD 495
Melt flow rate at 190 °C, 2.16 kg. (g/10 min)
ASTM D 1238
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.7
Tensile Modulus, 2% Secant(kg/cm2)
ASTM D 882
MD8300, TD10100
Tensile strength at Break(kg/cm2)
ASTM D 882
MD 470, TD 330
Thickness
(micron)
-
25
VICAT Softening Temperature
(°C)
ASTM D 1525
127
H6430BM
0.964
0.4
-
Description
EL-Lene™ H6430BM is a high density polyethylene resin which provides excellent stiffness, odorless, good processability, and printability.
Related Finished Products
Drinking water bottles, milk bottles
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.964
Flexural Modulus
(Mpa)
ASTM D 790
15000
IZOD
-
25
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.4
H655JA
0.955
0.4
-
Description
EL-Lene™ H655JA is a high density polyethylene resin with good processing performance and excellent mechanical properties. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
Related Finished Products
Caps and closures for carbonated soft drinks
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.955
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.4
H6670B
0.965
-
Description
EL-Lene™ H6670B is a high density polyethylene resin which provides good flowability, excellent stiffness, odorless, and good printability.
Related Finished Products
Milk bottles, juice bottles.
Properties
Test Methods
Value
Density (g/cm3)
ASTM D 1505
0.965
Flexural Modulus
(Mpa)
ASTM D 790
15000
Melt Index at 190 °C and 2.16 kg
(g/10 min)
ASTM D1238
Melt Index at 230 °C and 2.16 kg
(g/10 min)
ASTM D1238
0.7
S10
0.945
3.5
-
-
Description
S10 is a color compound high-density polyethylene (HDPE) for rotational moulding applications. S10 is designed for parts that require excellent stiffness and impact strength. It is fully heat and UV stabilized resulting in a wide processing latitude, good colour retention, and durability.
Related Finished Products
Underground water tanks, kayaks, superior rigidity, pallets, manholes
Properties
Test Methods
Value
ARM Impact Strength @ -40 °C, 5.5 mm rotomolded sample (J/mm)
Nowadays polyethylene has played an importance role in several pipeline industries such as water, gas, and mining pipe. SCG Chemicals is determined to create efficient plastic innovations to add value and create better living through relentlessly product development. An outstanding outcome is EL-Lene™ H112PC, a high performance material for high density polyethylene pipe.
As proven by accredited laboratory (EXOVA), pipes made from EL-Lene™ H112PC compound possesses impressive 10% higher withstanding pressure. With the benefit of superior strength, thickness of pipe using EL-Lene™ H112PC can be reduced by 10%. As a result, flow volume in operation increases. Besides, thinner wall also leads to easier to control pipe extrusion and faster welding installation.
In addition, slurry test showed that EL-Lene™ H112PC compound has 40% higher abrasion resistance than that of conventional PE100 pipe, and, as a consequence, has longer lifetime use.
EL-Lene™ H112PC compound is thus trusted for pipe in mining and water supply projects and is an ideal material for sustainable infrastructure.
To view VDO clickhttps://www.scgchemicals.com/en/news-media/media/video/17
To view product brochure and datasheet clickhttps://www.scgchemicals.com/en/products-services/product-type/pe/hdpe/grade/h112pc
Nowadays demand for disposable hygiene products, especially diapers and sanitary napkins, has increased dramatically in line with demographic changes in the world’s population. People these days are more concerned about hygiene, which has created higher competition among the manufacturers of this group of products. Producers thus have to adapt themselves and offer products with unique characteristics which will stand out from their competitors’. One characteristic that sells is softness. This makes customers feel more comfortable while wearing the product, and also does not irritate the skin.
Adding softness to nonwoven fabric used in the top sheet of a product which comes into direct contact with the users’ skin can be done by replacing the traditional PP spunbond with bi-component fiber. Thus, to adapt to market trends and better serve the needs of consumers, SCG Chemicals has striven to develop High-Density Polyethylene (HDPE) plastic pellets for use as the raw material in the manufacturing of bi-component fiber. The fiber is used as the “nonwoven” fabric on the top sheet of diapers or sanitary napkins which requires added softness.
Bi-component fiber’s structure is composed two layers. The core usually has Polypropylene (PP) or Polyethylene Tarephthalate (PET) as its main raw material where- as the sheath or the outer layer is coated with High-Density Polyethylene (HDPE) to give the fiber a softer feel while maintaining its other properties.
SCG Chemicals has developed EL-Lene H103S plastic pellets specifically for the production of bi-component fiber. In-depth research and development has resulted in a fiber that is softer and silkier than PP spunbond fiber. Apart from that, the bicomponent fiber also has other winning properties namely good elasticity, water absorbency and air permeability which re- duces the dampness of the nonwoven fabric top sheet of diapers and sanitary napkins. Also, it does not leave behind residues that may cause irritation to the skin.
Not only has EL-Lene H103S been created for use in bi-component fiber, it can also be used in staple fiber or other nonwoven fabrics that require added softness as well.
Bi-component fiber is an example of a product that results from SCG Chemicals’ ongoing commitment to developing products which best respond to customers’ needs.
Click here for more information aboutEL-Lene H103S
HDPE
Total 28 grades
EL-Lene™ HDPE is a high-density polyethylene resin produced by a bimodal process, a technology developed by Mitsui Chemicals Inc. of Japan.
EL-Lene™ H1000PBL is a blue (no lighter than RAL 5005), bimodal, high density polyethylene compound that is specially designed for water pressure pipes, especially for drinking water pipes. It is designed as PE100 pipes providing excellent in mechanical properties and processablitiy. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term use.
Related Finished Products
Drinking water pipe and stripe lines for PE100
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.951
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
EL-Lene™ H1000PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
EL-Lene™ H1000PCI is a black, bimodal technology, high density polyethylene compound designed for injection molding fitting. It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Related Finished Products
Injection grade for butt-fusion and electrofusion fittings
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.96
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
EL-Lene™ H1000PWI is a white HDPE compound using bimodal technology to provide superior mechanical properties, processablity, and low heat absorption. In addition, it has UV stabilizer and anti-oxidant package which combined with good dispersion of the white pigment results in excellent long term UV resistance and thermal stability.
Related Finished Products
Low heat absorption grade. Exernal coating for above ground pipe
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.972
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
EL-Lene™ H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology.It is classified as a MRS 11.2 material (PE112) which provides superior long - term hydro static strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides, it can be produced in all range of pipe diameters, recommended for the production of very thick wall and large diameter pipe.
EL-Lene™ H2001WC is a black bimodal high density polyethylene compound for jacketing in fiber optic and power cable applications. It contains well-dispersed carbon black of nominal particle size less than 20 nanometer to provide excellent weathering resistance and UV resistance.
Related Finished Products
Jacketing of fiber optic cables, Jacketing of power cables
EL-Lene™ H355JA is a high density polyethylene resin with good processability, mechanical property, and excellent organoleptic property. It is particularly designed for injection molding and continuous compression molding of caps and closures for the beverage packaging, especially for lightweight cap design.
Related Finished Products
Caps and closures for still and mineral water, juice, tea, and hot-filled beverages
EL-Lene™ H455JA is a high density polyethylene resin with good processability, mechanical property, and excellent organoleptic property. It is particularly designed for injection molding and continuous compression molding of caps and closures for the beverage packaging.
Related Finished Products
Caps and closures for still and mineral water, juice, and tea
EL-Lene™ H511W is a high density polyethylene resin for solid insulation in cable application. It is also suitable for outer skin in "foam-skin" constructions. It provides good performance across the full range of tele-communication insulation applications, including aircore and petroleum jelly filled cable designs in both buried and aerial environments.
EL-Lene™ H5211PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Related Finished Products
Drinking water, gas, conduit, corrugated pipes
Properties
Test Methods
Value
Density (g/cm3) (ISO 1183)
ISO 1183
0.96
Melt Index at 190 °C and 5.0 kg
(g/10 min)
ISO 1133
EL-Lene™ H555J is a high density polyethylene resin with good environmental stress cracking resistance, good processing performance, and organoleptic property. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures. Also, slip agent is contained to ensure easy-to-open.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
EL-Lene™ H555JA is a high density polyethylene resin with good environmental stress cracking resistance, good processing performance, organoleptic property. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
Related Finished Products
Caps and closures for carbonated soft drinks, hot fill beverages and water
EL-Lene™ H567J is a high density polyethylene resin with excellent processing performance and mechanical properties, especially for environmental stress cracking resistance. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures. It also contains slip agent ensuring easy opening.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
EL-Lene™ H567JA is a high density polyethylene resin with excellent processing performance and mechanical properties, especially for environmental stress cracking resistance. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
Related Finished Products
Caps and closures for carbonated soft drinks and hot fill beverages
EL-LeneTM H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process, this good flow ability grade designed for high productivity with good toughness product.
EL-Lene™ H5840B is a high density polyethylene resin which provides excellent ESCR, good surface appearance, good processability and good printability.
Related Finished Products
Chemical bottles, personal and homecare bottles, lube oil bottles
EL-Lene™ H6140B is a high density polyethylene resin which provides excellent surface appearance, good impact strength, processability and printability.
EL-LeneTM H619F is a high stiff homopolymer HDPE designed to improve film stiffness and barrier properties when co-extruded with LLDPE & LDPE. It also provides good film clarity and processability when used in the core layer with an excellent compatibility with LLDPE & LDPE.
EL-Lene™ H655JA is a high density polyethylene resin with good processing performance and excellent mechanical properties. It is particularly designed for injection molding and continuous compression molding of beverage caps and closures.
S10 is a color compound high-density polyethylene (HDPE) for rotational moulding applications. S10 is designed for parts that require excellent stiffness and impact strength. It is fully heat and UV stabilized resulting in a wide processing latitude, good colour retention, and durability.
Related Finished Products
Underground water tanks, kayaks, superior rigidity, pallets, manholes
Properties
Test Methods
Value
ARM Impact Strength @ -40 °C, 5.5 mm rotomolded sample (J/mm)
Nowadays polyethylene has played an importance role in several pipeline industries such as water, gas, and mining pipe. SCG Chemicals is determined to create efficient plastic innovations to add value and create better living through relentlessly product development. An outstanding outcome is EL-Lene™ H112PC, a high performance material for high density polyethylene pipe.
As proven by accredited laboratory (EXOVA), pipes made from EL-Lene™ H112PC compound possesses impressive 10% higher withstanding pressure. With the benefit of superior strength, thickness of pipe using EL-Lene™ H112PC can be reduced by 10%. As a result, flow volume in operation increases. Besides, thinner wall also leads to easier to control pipe extrusion and faster welding installation.
In addition, slurry test showed that EL-Lene™ H112PC compound has 40% higher abrasion resistance than that of conventional PE100 pipe, and, as a consequence, has longer lifetime use.
EL-Lene™ H112PC compound is thus trusted for pipe in mining and water supply projects and is an ideal material for sustainable infrastructure.
To view VDO clickhttps://www.scgchemicals.com/en/news-media/media/video/17
To view product brochure and datasheet clickhttps://www.scgchemicals.com/en/products-services/product-type/pe/hdpe/grade/h112pc
Nowadays demand for disposable hygiene products, especially diapers and sanitary napkins, has increased dramatically in line with demographic changes in the world’s population. People these days are more concerned about hygiene, which has created higher competition among the manufacturers of this group of products. Producers thus have to adapt themselves and offer products with unique characteristics which will stand out from their competitors’. One characteristic that sells is softness. This makes customers feel more comfortable while wearing the product, and also does not irritate the skin.
Adding softness to nonwoven fabric used in the top sheet of a product which comes into direct contact with the users’ skin can be done by replacing the traditional PP spunbond with bi-component fiber. Thus, to adapt to market trends and better serve the needs of consumers, SCG Chemicals has striven to develop High-Density Polyethylene (HDPE) plastic pellets for use as the raw material in the manufacturing of bi-component fiber. The fiber is used as the “nonwoven” fabric on the top sheet of diapers or sanitary napkins which requires added softness.
Bi-component fiber’s structure is composed two layers. The core usually has Polypropylene (PP) or Polyethylene Tarephthalate (PET) as its main raw material where- as the sheath or the outer layer is coated with High-Density Polyethylene (HDPE) to give the fiber a softer feel while maintaining its other properties.
SCG Chemicals has developed EL-Lene H103S plastic pellets specifically for the production of bi-component fiber. In-depth research and development has resulted in a fiber that is softer and silkier than PP spunbond fiber. Apart from that, the bicomponent fiber also has other winning properties namely good elasticity, water absorbency and air permeability which re- duces the dampness of the nonwoven fabric top sheet of diapers and sanitary napkins. Also, it does not leave behind residues that may cause irritation to the skin.
Not only has EL-Lene H103S been created for use in bi-component fiber, it can also be used in staple fiber or other nonwoven fabrics that require added softness as well.
Bi-component fiber is an example of a product that results from SCG Chemicals’ ongoing commitment to developing products which best respond to customers’ needs.
Click here for more information aboutEL-Lene H103S