GRADE

P901J

SCGC™ P901J is polypropylene homopolymer with excellent flowability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding.

Properties	Test Methods	Value	Unit
Melt Flow Rate at 230 °C and 2.16 kg	ASTM D 1238	70	g/10 min
Density	ASTM D 1505	0.910	g/cm³
Heat Deflection Temperature at 4.6 kg/cm²	ASTM D 648	125	°C
Tensile Strength at Yield	ASTM D 638 @ Crosshead speed 50 mm/min	360	kg/cm²
Flexural Modulus	ASTM D 790	16,500	kg/cm²
Izod Impact Strength at 23°C	ASTM D 256	38	J/m
%Shrinkage (2mm) MD	TPE Method	1.00	%
%Shrinkage (2mm) TD	TPE Method	1.25	%
Haze	ASTM D 1003	35	%

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P441JU is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process and recommended for product that requires good impact strength and stiffness balance.

SCGC™ PP P483JU is a developmental of high stiffness polypropylene impact copolymer product which contains anti-static agent and UV stabilizer. It is designed for very high stiffness, creep resistance, and high heat resistance while maintain a good impact strength than those of general impact copolymer polypropylene and suitable for injection molding application.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P642J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is suitable for Injection molding process. This resin is recommended for product that requires high impact strength and stiffness.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

SCGC™ PP P840J is a high flow ability impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P841J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires very high processability and good UV performance.

SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

SCGC™ M735RU is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RU is a natural PE resin available in a pellet form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of decorative items and small industrial parts.

SCGC™ M735RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RW is a natural PE resin available in a pellet form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ PP P1085J is high crystalline polypropylene impact copolymer. It is designed for compounding base. This resin is recommended for automotive and appliance compounding products that require high melt flow rate for thin wall parts.

SCGC™ PP P639AT is very high flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is suggested for compounds that require low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P739ET is high flowability polypropylene impact copolymer. It is designed for compounding base and injection molding process. This resin is recommended for compounds that require good surface aesthetics and low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P747WT is low gloss and medium flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is recommended for product which require good surface aesthetics and stiffness/impact balance. It is suitable for various automotive parts.

SCGC™ PP P765J is very high impact polypropylene copolymer. It is designed for automotive interior and exterior parts such as door trims, instrumental panel and bumper which it’s suitable for injection molding process. This resin is recommended for product that require very high impact strength at room temperature and low temperature.

PF682 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

SCGC™ PVC PF741 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG680 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG740 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG770 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

S411B is a high strength polyethylene resin designed for small blow molding containers (size up to 6 L). This grade provides excellent combination of stiffness and chemical resistance for light weight container.

SCGC™ S495B is a high strength polyethylene resin designed to provides excellent combination of stiffness and chemical resistance for blow molding container size upto 30L

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

SCGC™ PP X811T is high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

SCGC™ PP X861T is a high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

PCDH02BW is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

SCGC PP P1088J is a high flowability and high crystalline polypropylene impact copolymer which designed for thin wall injection molding.

SCGC PP P341S is an impact copolymer polypropylene with low flowability.

SCGC GREEN POLYMER™ Circular Polypropylene A10P740J is contained 10% recycling content derived from advanced recycling technology that turn post-consumer plastics into recycled feedstock for virgin like plastic production. A10P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC PP, P140S is an impact copolymer polypropylene with very low flowability

SCGC™ LLDPE M70 series is color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ PVC PR701 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC PP P1000J is a very high-flowability and high-crystallinity homopolymer polypropylene designed to optimize flow and stiffness performance for automotive compounding applications requiring thin-walled injection molding. It is also suitable as a base resin for fiber-reinforced polypropylene composites.

SCGC™ M1FBKA2P is a black, halogenated, polyethylene (PE)-based compound designed for rotational molding applications. It meets the UL 94 V-2 flame retardancy standard, UL 746A, and includes a UV stabilizer package for long-lasting performance in both indoor and outdoor environments.

SCGC™ M735RWP is the powder form of M735RW, a linear low-density polyethylene (LLDPE) grade designed for rotational moulding applications. Offering high melt flow and an excellent balance of impact strength, stiffness, and processability, this grade is ideal for lawn and garden articles, decorative items, and small industrial parts.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC GREEN POLYMER™ PCDP02JN is a certified odorless Post-Consumer Recycled Resin impact copolymer polypropylene. This grade is suitable for injection molding application. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMER™ PCRP03JB is a certified Post-Consumer Recycled Resin impact copolymer polypropylene. This grade is suitable for injection molding application. This product is not intended for food contact, pharmaceutical or medical applications.