SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

Properties	Test Methods	Value
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D 1238	30.00
Tensile Strength at Yield (MPa)	ASTM D 638 @ Crosshead speed 50 mm/min	28
Flexural Modulus (kg/cm²)	ASTM D 790	14,500
Izod Impact Strength at 23°C (J/m)	ASTM D 256	78
Izod Impact Strength at 0 °C (J/m)	ASTM D 256	55
Izod Impact Strength at -20 °C (J/m)	ASTM D 256	41

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูงที่เหมาะแก่การนำไปขึ้นรูปเป็นขวดบรรจุสารเคมีโดยกระบวนการเป่าขึ้นรูป

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ พีพี P400S เป็นพอลิโพรพิลีนชนิดโฮโมพอลิเมอร์ ที่ถูกออกแบบสำหรับกระบวนการอัดรีดด้วยหัวดายแบบ T-die หรือแบบ spinneret ซึ่งเหมาะสำหรับการผลิตเส้นด้ายแบนหรือเส้นใยเดี่ยว โดยมีจุดเด่นในเรื่องการขึ้นรูปที่สม่ำเสมอ ให้อัตราผลผลิตสูงและสมบัติเชิงกลที่ดี

SCGC™ พีพี P401S เป็นพอลิโพรพิลีนชนิดโฮโมพอลิเมอร์ ที่ถูกออกแบบสำหรับกระบวนการอัดรีดด้วยหัวดายแบบ T-die หรือแบบ spinneret ซึ่งเหมาะสำหรับการผลิตเส้นด้ายแบนหรือเส้นใยเดี่ยว โดยมีจุดเด่นในเรื่องการขึ้นรูปที่สม่ำเสมอและสมบัติเชิงกลที่ดีเยี่ยม

SCGC™ พีพี P403J เป็นเม็ดพลาสติกพอลิโพรพิลีน ชนิด homopolymer ที่เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป

SCGC™ พีพี P440J เม็ดพลาสติกพอลิโพรพิลีนบล็อกโคพอลิเมอร์ เหมาะสำหรับกระบวนการฉีดขึ้นรูปและเหมาะกับผลิตภัณฑ์ที่ต้องการความแข็งแรงและทนแรงกระแทก

SCGC™ พีพี P441JU เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีสารป้องกันไฟฟ้าสถิตย์และสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการความต้านทานแรงกระแทกสูงและใช้งานภายนอกอาคาร

SCGC™ พีพี P483JU เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีสารป้องกันไฟฟ้าสถิตย์และสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการความแข็งแรงสูง และต้านทานแรงกระแทกสูง อีกทั้งยังทนต่อแสงแดดภายนอกอาคาร

SCGC™ พีพี P640J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ เหมาะสำหรับกระบวนการฉีดขึ้นรูปและเหมาะกับผลิตภัณฑ์ที่ต้องการความแข็งแรงและทนแรงกระแทก

SCGC™ พีพี P642J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีสารป้องกันไฟฟ้าสถิตย์และสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการความแข็งแรงและทนต่อแรงกระแทก

SCGC™ พีพี P686J เม็ดพลาสติกพอลิโพรพิลีนบล็อกโคพอลิเมอร์ที่มีการเติมสารก่อผลึก ถูกพัฒนาขึ้นสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการคุณสมบัติทนแรงกระแทกสูง มีความแข็งทรงรูป และมีอัตราการผลิตที่ดี

SCGC™ พีพี P700J เป็นเม็ดพลาสติกพอลิโพรพิลีน ชนิด homopolymer ที่เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป

SCGC™ พีพี P701J เป็นเม็ดพลาสติกพอลิโพรพิลีน ชนิด homopolymer ที่เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป

SCGC™ พีพี P702J เป็นเม็ดพลาสติกพอลิโพรพิลีน ชนิด homopolymer ที่เหมาะสำหรับกระบวนการฉีดขึ้นรูป และเหมาะกับผลิตภัณฑ์ทั่วไปที่ต้องการความแข็งแรงสูงและต้องการความใส

SCGC™ พีพี P722JO เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานฝาและกล่องแบตเตอรี่

SCGC™ พีพี P740J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ เหมาะสำหรับกระบวนการฉีดขึ้นรูปและเหมาะกับผลิตภัณฑ์ที่ต้องการความแข็งแรงและทนแรงกระแทก

SCGC™ พีพี P744J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ เหมาะสำหรับกระบวนการฉีดขึ้นรูปที่ต้องการความรวดเร็วและชิ้นงานมีความแข็งแรงสูง

SCGC™ พีพี P750J เม็ดพลาสติกพอลิโพรพิลีนที่มีความใส และใส่สารป้องกันไฟฟ้าสถิตย์ เหมาะสำหรับการฉีดขึ้นรูปชิ้นงานที่ต้องการความใส

SCGC™ พีพี P840J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีความสามารถในการไหลตัวได้ดี เหมาะสำหรับกระบวนการฉีดขึ้นรูปและเหมาะกับผลิตภัณฑ์ที่ต้องการความแข็งแรงและทนแรงกระแทก

SCGC™ พีพี P841J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ที่มีการเติมสารป้องกันไฟฟ้าสถิตย์และสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปที่ต้องการความรวดเร็วและชิ้นงานทนต่อแสงแดดภายนอกอาคาร

SCGC™ พีพี P842J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ เหมาะสำหรับกระบวนการฉีดขึ้นรูปที่ต้องการความรวดเร็วและชิ้นงานมีความแข็งแรงสูงมาก

SCGC™ พีพี P851JO เป็นเม็ดพลาสติกพอลิโพรพิลีนที่มีความใส เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูปที่ต้องการความใสสูง อัตราผลผลิตสูง และมีสารป้องกันไฟฟ้าสถิตย์

SCGC™ พีพี P945J เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ ไหลตัวดี เพื่อลดของเสียจากรอยขาวเนื่องจากความเค้นในกระบวนการผลิต อีกทั้งยังมีความสมดุลย์ในเรื่องของการทนแรงกระแทก และความแข็งแรง สำหรับการผลิตสินค้าของใช้ในบ้าน

SCGC™ SMX551BU เป็นเม็ดพลาสติกพอลิเอทีลีนที่มีความแข็งแรงสูง ผลิตด้วยเทคโนโลยี SMX™ ซึ่งเหมาะสำหรับการผลิตบรรจุภัณฑ์ชนิด IBC (Intermediate Bulk Containers) เกรดนี้สามารถรักษาความแข็งแรงที่สูงขณะหลอมทำให้เกิดประสิทธิภาพที่ดีในการผลิต เกิดกลิ่นและควันที่น้อยมาก อีกทั้งคุณณสมบัติในการทนทานต่อสารเคมีได้ดีเยี่ยมและยังคงความแข็งแรงได้เป็นอย่างดี

SCGC™ เอชดีพีอี F15 เม็ดพลาสติกพีอีชนิดความหนาแน่นสูงที่ถูกออกแบบมาสำหรับฟิล์มหน้ากว้างและเครื่องเป่าฟิล์มที่มีกำลังการผลิตสูง คุณสมบัติเด่นคือ การทนแรงดึงยืด และกำลังการผลิตสูง

SCGC™ เอชดีพีอี H377C เม็ดพอลิเอทิลีนความหนาแน่นสูง สำหรับคาสท์ฟิล์ม งานเคลือบและงานลามิเนต ที่ให้สมบัติด้านความแข็ง การทนต่อความร้อน และ การป้องกันรอยขีดข่วนที่ดีเยี่ยม

SCGC™ เอชดีพีอี H5480S เป็นพอลิเอทิลีนความหนาแน่นสูง ที่ถูกออกแบบสำหรับกระบวนการอัดรีดด้วยหัวดายแบบ spinneret หรือแบบ T-die ซึ่งเหมาะสำหรับการผลิตเส้นใยเดี่ยวหรือเส้นด้ายแบน โดยมีจุดเด่นในเรื่องความสมดุลระหว่างการขึ้นรูปและสมบัติเชิงกลที่ดี

SCGC™ เอชดีพีอี H5604F เม็ดพลาสติกพีอีชนิดความหนาแน่นสูงที่ถูกออกแบบมาสำหรับการผลิตฟิล์มคุณภาพสูงที่ต้องการการทรงรูป และการทนแรงดึง สามารถใช้งานได้กับฟิล์มหลากหลายประเภท

SCGC™ เอชดีพีอี H5814J เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูง เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป และมีความสามารถในการไหลตัวได้ดีซึ่งจะช่วยในเรื่องอัตราการผลิตที่สูง อีกทั้งมีความเหนียวที่ดี

SCGC™ เอชดีพีอี H5818J เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูง เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป และมีความสามารถในการไหลตัวได้ดีซึ่งจะช่วยในเรื่องอัตราการผลิตที่สูง

SCGC™ เอชดีพีอี H6105JU เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูงที่มีคุณสมบัติความแข็งแรงเชิงกลที่ดี มีความแข็งคงรูปสูงและทนแรงกระแทก พร้อมเติมสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปสินค้าอุตสาหกรรม

SCGC™ เอชดีพีอี H6140B เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูงที่เหมาะแก่การนำไปขึ้นรูปเป็นบรรุภัณฑ์เครื่องสำอางโดยกระบวนการเป่าขึ้นรูป

SCGC™ เอชดีพีอี H619F เม็ดพอลิเอทิลีนความหนาแน่นสูงสำหรับงานเป่าฟิล์มและฟิล์มชนิดพิเศษแบบดึงยืดในแนวของเครื่องจักรที่ให้คุณสมบัติด้านการกันความชื้น การทนต่อความร้อน และความแข็งที่ดี เมื่อผสมกับเม็ดพอลิเอทิลีนความหนาแน่นต่ำและเม็ดพอลิเอทิลีนความหนาแน่นต่ำเชิงเส้น

SCGC™ เอชดีพีอี H6308JU เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นสูงที่มีคุณสมบัติการไหลตัวที่ดี พร้อมเติมสารป้องกันรังสีอัลตราไวโอเลต เหมาะสำหรับกระบวนการฉีดขึ้นรูปสินค้าอุตสาหกรรม

SCGC™ แอลแอลดีพีอี L1210F เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยมีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการการเปิกปากถุงที่ง่าย และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L1211FA เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยไม่มีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการความใส และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L1220F เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยมีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการการเปิกปากถุงที่ง่าย และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L1221FA เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยไม่มีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการความใส และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L1810FI เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยมีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติดในปริมาณที่ถูกออกแบบมาสำหรับงานเป่าฟิล์มผ่านน้ำ เพื่อให้ได้ฟิล์มที่มีความใสและมีการเปิดปากถุงที่ง่าย

SCGC™ แอลแอลดีพีอี L2009F เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยมีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการการเปิกปากถุงที่ง่าย และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L2009FA เม็ดพลาสติกพีอีชนิดความหนาแน่นต่ำเชิงเส้น โดยไม่มีสารเติมแต่งประเภทสารทำให้ลื่นและสานป้องกันการยึดติด เหมาะสำหรับฟิล์มพลาสติกทั่วไปที่ต้องการความใส และสามารถนำไปผสมกับเม็ดพลาสติกชนิด HDPE และ LDPE

SCGC™ แอลแอลดีพีอี L2420J เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นต่ำเชิงเส้น เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป ถูกพัฒนาขึ้นสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการคุณสมบัติทนแรงกระแทกสูง และมีความสามารถในการทนสารเคมีที่ดี

SCGC™ แอลแอลดีพีอี L2650J เป็นเม็ดพลาสติกพอลิเอทิลีนชนิดความหนาแน่นต่ำเชิงเส้น เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูป ถูกพัฒนาขึ้นสำหรับกระบวนการฉีดขึ้นรูปชิ้นงานที่ต้องการคุณสมบัติทนแรงกระแทกสูง และมีความสามารถในการทนสารเคมีที่ดี

SCGC™ M3565RW is a lilinear-low density polyethylene (LLDPE) with Hexene co-monomer (C6) for rotational moulding. M3565RW is a natural color PE resin aviailable in a pellet form.With a high UV resistance (8), good balancing of stiffness & impact, excellent surface finishing, good dimension tolerance and excellent ESCR, this grade suitable for rototional moulding of water tanks, chemical tanks and Automotive parts.

SCGC™ LLDPE M70 series are color powder of linear-low density polyethylene (LLDPE) for rotational moulding applications. M70 series are high melt flow and a balance of impact strength, stiffness, and processability, these grades are suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ M735RU is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RU is a natural color PE resin available in a pellet and powder form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of decorative items and small industrial parts.

SCGC™ M735RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RW is a natural color PE resin available in a pellet and powder form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ PP P1085J is high crystalline polypropylene impact copolymer. It is designed for compounding base. This resin is recommended for automotive and appliance compounding products that require high melt flow rate for thin wall parts.

SCGC™ PP P639AT is very high flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is suggested for compounds that require low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P739ET is high flowability polypropylene impact copolymer. It is designed for compounding base and injection molding process. This resin is recommended for compounds that require good surface aesthetics and low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P747WT is low gloss and medium flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is recommended for product which require good surface aesthetics and stiffness/impact balance. It is suitable for various automotive parts.

SCGC™ PP P765J is very high impact polypropylene copolymer. It is designed for automotive interior and exterior parts such as door trims, instrumental panel and bumper which it’s suitable for injection molding process. This resin is recommended for product that require very high impact strength at room temperature and low temperature.

SCGC™ พีพี P838C คือพอลิโพรพิลีนที่ถูกออกแบบมาสำหรับการเคลือบหรือการลามิเนตกับพื้นผิวที่ทำจากพอลิพอพิลีนที่ต้องการความแข็งและความทรงรูปของผลิตภัณฑ์ เช่น การเคลือบกระสอบ ผ้าใบ การลามิเนตกับพื้นผิวที่ทำจากพอลิพอพิลีน เช่น กระดาษฟิล์ม OPP หรือ BOPP

SCGC™ P901J is polypropylene homopolymer with excellent flowability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding.

SCGC™ พีวีซี PC750 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลสูง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PF621 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลปานกลาง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PF682 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลปานกลาง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PF741 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลสูง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PG680 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลปานกลาง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PG740 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลสูง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

SCGC™ พีวีซี PG770 เป็นพีวีซีโฮโมพอลิเมอร์สำหรับการใช้งานแบบ Paste ซึ่งมีน้ำหนักโมเลกุลสูง ผลิตโดย TPC Paste Co. , Ltd. ภายใต้เทคโนโลยี HYBRID ของ OxyChem

S111F เป็นเม็ดพลาสติกพอลิเอทีลีนที่มีความแข็งแรงสูง ผลิตด้วยเทคโนโลยี SMX ซึ่งมีความเหนี่ยวและความทรงรูปสูง สามารถใช้ผลิตในกระบวนการเป่าฟิล์มที่ให้กำลังการผลิตสูง และสามารถขึ้นรูปได้ง่าย เกรดนี้เหมาะสำหรับการทำฟิล์มคุณภาพสูงที่ใช้งานในอุตสาหกรรม

SCGC™ HDPE S16 is a color compound high-density polyethylene (HDPE) for rotational moulding applications. S16 is designed for parts that require excellent stiffness and impact strength. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and durability.

S199F เป็นเม็ดพลาสติกพอลิเอทีลีนที่มีความแข็งแรงสูง ผลิตด้วยเทคโนโลยี SMX ทำให้มีคุณสมบัติด้านการทนแรงกระแทกดีและมีความสามารถในการใช้งานในการขึ้นรูปที่ดีเยี่ยม เม็ดพลาสติกเกรดนี้สามารนำไปใช้งานในการขึ้นรูปเป็นฟิล์มได้หลากหลาย ที่หลายความกว้าง และหลายสภาวะการผลิตโดยที่ยังให้คุณสมบัติต่างๆของฟิล์มดีและการขึ้นรูปง่าย เม็ดพลาสติกเกรดนี้เหมาะสำหรับการทำฟิล์มคุณภาพสูงที่ใช้งานสำหรับผู้บริโภค และอุตสาหกรรม เช่นถุงฟลาสติกทั่วไป

SCGC™ S411B เม็ดพลาสติกพอลิเอทิลีนความหนาแน่นสูงที่มีความแข็งแรงสูง สำหรับบรรจุภัณฑ์ที่มาจากกระบวนการเป่า มีคุณสมบัติช่วยลดน้ำหนักบรรจุภัณฑ์โดยยังคงความแข็งแรงและความทนต่อสารเคมีได้เป็นอย่างดี

SCGC™ S495B เม็ดพลาสติกพอลิเอทิลีนความหนาแน่นสูงที่มีความแข็งแรงสูง สำหรับบรรจุภัณฑ์ที่มาจากกระบวนการเป่า มีคุณสมบัติความแข็งแรงและความทนต่อสารเคมีได้เป็นอย่างดี

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลต่ำ ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลต่ำ ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลปานกลาง ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลสูง ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลสูง ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

พีวีซีเรซินโฮโมพอลิเมอร์ น้ำหนักโมเลกุลสูง ลักษณะเป็นผงร่วนสีขาว ผลิตจากกระบวนการพอลิเมอร์ไรเซชันแบบแขวนลอย ผงพีวีซีเรซินสามารถผสมกับสารเติมแต่งอื่นๆ ได้เป็นอย่างดี เพื่อให้ได้คุณสมบัติของสินค้าสำเร็จรูปตามที่ต้องการ

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC™ PP X811T is high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

SCGC™ PP X861T is a high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

60701WHA เป็นผลิตภัณฑ์เทอร์โมพลาสติกพอลิโอเลฟินคอมพาวน์ โดยสินค้านี้ออกแบบมาสำหรับขึ้นรูปผ่านกระบวนการรีดออกมาเป็นซีล หรือขอบยางสำหรับอุปกรณ์ไฟฟ้า

เม็ดพลาสติกเกรด PCRH01BN เป็นเม็ดพลาสติกรีไซเคิลพอลิเอททิลีนชนิดความหนาแน่นสูงที่ผ่านการรับรองการผลิตซึ่งเหมาะกับการขึ้นรูปโดยวิธีการเป่าด้วยแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCRH02BW เป็นเม็ดพลาสติกรีไซเคิลชนิดพอลิเอททิลีนความหนาแน่นสูงที่ผ่านการรับรองการผลิตซึ่งเหมาะกับการขึ้นรูปโดยวิธีการเป่าด้วยแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCRH03BB เป็นเม็ดพลาสติกรีไซเคิลพอลิเอททิลีนชนิดความหนาแน่นสูงที่ผ่านการรับรองการผลิตซึ่งเหมาะกับการขึ้นรูปโดยวิธีการเป่าด้วยแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCRP01JN เป็นเม็ดพลาสติกรีไซเคิลพอลิโพรลีนที่ผ่านการรับรองการผลิตซึ่งเหมาะกับการขึ้นรูปโดยวิธีการฉีดในแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCDH01BN เป็นเม็ดพลาสติกรีไซเคิลชนิดพอลิเอททิลีนความหนาแน่นสูงที่ผ่านการรับรองการผลิตที่ใช้เทคโนโลยีกระบวนการลดกลิ่นของเม็ดพลาสติก ซึ่งเหมาะกับการขึ้นรูปโดยวิธีการเป่าด้วยแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCDH02BW เป็นเม็ดพลาสติกรีไซเคิลชนิดพอลิเอททิลีนความหนาแน่นสูงที่ผ่านการรับรองการผลิตที่ใช้เทคโนโลยีกระบวนการลดกลิ่นของเม็ดพลาสติก ซึ่งเหมาะกับการขึ้นรูปโดยวิธีการเป่าด้วยแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี กรีนพอลิเมอร์ เกรด PCDP01JN เป็นเม็ดพลาสติกรีไซเคิลพอลิโพรลีนที่ผ่านการรับรองการผลิตที่ใช้เทคโนโลยีกระบวนการลดกลิ่นของเม็ดพลาสติก ซึ่งเหมาะกับการขึ้นรูปโดยวิธีการฉีดในแม่พิมพ์ แต่ผลิตภัณฑ์ที่ได้จากการขึ้นรูปยังไม่สามารถใช้กับเกรดที่สัมผัสกับอาหารและยาได้

เอสซีจีซี พีพี P951J เป็นเม็ดพลาสติกพอลิโพรพิลีน ชนิด random copolymer เหมาะสำหรับผลิตภัณฑ์ทั่วไปที่ผลิตจากกระบวนการฉีดขึ้นรูปที่ต้องการความใสสูง อัตราผลผลิตสูง และมีสารป้องกันไฟฟ้าสถิตย์

แอคทีฟพลัส เกรด SB31L เป็นสารที่ทำให้ลื่นและป้องกันการยึดติด โดยมีปริมาณสารตัวช่วยในอัตราส่วนที่เหมาะสม ซึ่งจะช่วยให้ฟิล์มแยกออกจากกันได้ง่ายขึ้น ส่งผลต่อการเปิดปากถุงที่ดีขึ้น

แอคทีฟพลัส เกรด SB32L เป็นสารที่ทำให้ลื่นและป้องกันการยึดติด โดยมีปริมาณสารตัวช่วยในอัตราส่วนที่สูง ซึ่งจะช่วยให้ฟิล์มแยกออกจากกันได้ง่ายขึ้น ส่งผลต่อการเปิดปากถุงที่ดีขึ้น

แอคทีฟพลัส เกรด PA17L เป็นสารที่ช่วยในกระบวนการขึ้นรูป โดยสารนี้จะสร้างสารเคลือบหล่อลื่นบนผิววัสดุของเครื่องมือบริเวณสกรูและดาย ซึ่งจะทำให้ผิวของชิ้นงานมีความเรียบเนียน ไม่ขรุขระ สามารถลดปริมาณของเสียได้

SCGC PP P1088J is a high flowability and high crystalline polypropylene impact copolymer which designed for thin wall injection molding.

SCGC PP P341S เม็ดพลาสติกพอลิโพรพิลีนอิมแพ็คโคพอลิเมอร์ที่มีความสามารถในการไหลต่ำ

SCGC SOLUTIONS

Industrial Packaging

Storage and Container

Household Products

Home Appliances

Recreational & Decorative Products

Automotive Parts