close

GRADE

S199F

S199F is a high strength polyethylene produced by SMX™ technology, resulting in better impact strength with excellent process ability. This grade can be produced various film widths from wider operating condition with balancing between mechanical properties and bubble stability. It is recommended for high quality film application in consumer and industrial segment such as general purpose film.

Properties	Test Methods	Value	Unit
Density	ASTM D 1505	0.956	g/cm³
Melt Flow Rate at 190 °C and 2.16 kg	ASTM D 1238	0.04	g/10 min
Tensile strength at Break	ASTM D 882	MD 1100, TD 720	kg/cm²
Dart Impact Strength	ASTM D 1709	280	g
Tear Strength	-	MD 6, TD 40	MD/TD
US FDA 21 CFR 177.1520	-	✓

Environmental Profile

*Benchmark = Thailand Greenhouse Gas Management Organization (TGO)

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ HDPE F15 is a high density polyethylene product of bi-modal process. It is recommended for film which is produced by high speed machine and wide lay flat. The key characteristics are high tesile strength and high productivity.

SCGC™ HDPE H5604F is a high density polyethylene product of bi-modal process which suitable for the high quality film application. It is recommended for general purpose film with high tensile strength.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P601F is a homopolymer polypropylene resin for water-quenched blown film.This grade is contain high slip and antiblock agent and recommended for applications that film thickness is lower than 50 micron.

SCGC™ PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. This grade is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

PCRH01BN is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

PCRH02BW is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

PCRH03BB is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH01BN is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH02BW is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in openability while yielding higher cost efficiency.

Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result is a significant improvement in openability while yielding higher cost efficiency.

Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.

SCGC HDPE S521B is an extra high molecular weight high density polyethylene resin produced by SMX technology for producing chemical and food containers 20-30 litres and other large blow molding applications by blow molding process. This grade provides excellent combination of stiffness and impact strength with good processability.

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCG GREEN POLYMER™ grade PCDL01FN is a 100% certified Post-Consumer Recycled linear-low density polyethylene resin. This grade is suitable for LLDPE film application. This product is suitable for applied as film packaging and not intended for direct food contact, pharmaceutical or medical applications.

Active Plus™ PA18L is a non - fluorinated processing aids masterbatch (PFAS free) which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface. PA18L creates lubricity coating on the metallic surfaces of processing equipment like barrel and die surfaces. The coating decreases the friction between molten resin and die wall then resulting in surface defects (shark skin and melt fracture elimination).

Market & Application

Innovation and Technology Solution