GRADE

A10P740J

Properties Test Methods Value Unit
Melt Flow Rate at 230 °C and 2.16 kg ASTM D 1238 27 g/10 min
Density ASTM D 1505 0.91 g/cm³
Melting Point ASTM D 2117 163 °C
VICAT Softening Temperature ASTM D 1525 150 °C
HDT at 4.6 kg/cm² ASTM D 648 110 °C
Tensile Strength at Yield ASTM D 638 @ Crosshead speed 50 mm/min 290 kg/cm²
Flexural Modulus ASTM D 790 12,500 kg/cm²
Notched Izod Impact Strength ASTM D 256 @ 23°C 78 J/m
Notched Izod Impact Strength ASTM D 256 @ 0°C 49 J/m
Notched Izod Impact Strength ASTM D 256 @ -20°C 39 J/m
Rockwell Hardness ASTM D 785 70 R-Scale
%Shrinkage (2mm) MD TPE Method 1.4 %
%Shrinkage (2mm) TD TPE Method 1.2 %
Flammability UL-94 HB -