GRADE

AP945J

Properties	Test Methods	Value	Unit
Melt Flow Rate at 230 °C and 2.16 kg	ASTM D 1238	65	g/10 min
Tensile Strength at Yield	ASTM D 638 @ Crosshead speed 50 mm/min	270	kg/cm²
Flexural Modulus	ASTM D 790	14,000	kg/cm²
Izod Impact Strength at 23°C	ASTM D 256	65	J/m

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P403J is a homopolymer polypropylene resin suitable for general propose product which required good impact resistance produced from injection molding process.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P441JU is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process and recommended for product that requires good impact strength and stiffness balance.

SCGC™ PP P483JU is a developmental of high stiffness polypropylene impact copolymer product which contains anti-static agent and UV stabilizer. It is designed for very high stiffness, creep resistance, and high heat resistance while maintain a good impact strength than those of general impact copolymer polypropylene and suitable for injection molding application.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P642J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is suitable for Injection molding process. This resin is recommended for product that requires high impact strength and stiffness.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P700J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process from SCG.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P722JO is polypropylene impact copolymer which contains UV stabilizer. This resin is recommended for producing battery case from injection molding process.

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P840J is a high flow ability impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P841J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires very high processability and good UV performance.

SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

SCGC™ LLDPE M3504DXP is powder of a linear low density polyethylene octene copolymer for rotational molding applications. M3504DXP are specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks with a generous radius and curve.

SCGC™ LLDPE M3804RU is a linear-low density polyethylene (LLDPE) for indoor / semi-indoor rotational moulding applications. M3804RU is a natural PE resin available in a pellet form. This grade is suitable for rotational moulding of storage tanks and general-purpose applications which are indoor / semi-indoor or for thin wall (less than 5 mm) parts.

SCGC™ LLDPE M3804RW is linear low density polyethylene (LLDPE) for rotational molding applications. M3804RW is a natural PE resin available in a pellet form. These grades are suitable for rotational molding of storage tanks and general applications.

SCGC™ LLDPE M40 are color compound linear-low density polyethylene (LLDPE) for rotational molding applications. These grades are suitable for containers and general applications which have wall thickness less than 5 mm. M40 has UV8 protection for outdoor application.

SCGC™ M735RU is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RU is a natural PE resin available in a pellet form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of decorative items and small industrial parts.

SCGC™ M735RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M735RW is a natural PE resin available in a pellet form. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ LLDPE M9001RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M9001RW is a natural PE resin available in a pellet form. This grade is suitable for rotational moulding of large water tanks and parts that require high stiffness.

SCGC™ PP P1085J is high crystalline polypropylene impact copolymer. It is designed for compounding base. This resin is recommended for automotive and appliance compounding products that require high melt flow rate for thin wall parts.

SCGC™ PP P639AT is very high flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is suggested for compounds that require low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P739ET is high flowability polypropylene impact copolymer. It is designed for compounding base and injection molding process. This resin is recommended for compounds that require good surface aesthetics and low flow mark after injection process. It is suitable for various automotive parts.

SCGC™ PP P747WT is low gloss and medium flowability polypropylene impact copolymer. It is designed for compounding and injection molding process. This resin is recommended for product which require good surface aesthetics and stiffness/impact balance. It is suitable for various automotive parts.

SCGC™ PP P765J is very high impact polypropylene copolymer. It is designed for automotive interior and exterior parts such as door trims, instrumental panel and bumper which it’s suitable for injection molding process. This resin is recommended for product that require very high impact strength at room temperature and low temperature.

SCGC™ P901J is polypropylene homopolymer with excellent flowability, high stiffness and high clarity. This grade is especially suitable for thin wall injection molding.

SCGC™ PVC PC750 is a high molecular weight homoploymer paste PVC resin, produced by TPC Paste Co.,Ltd. under OxyChem's HYBRID technology

PF621 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

PF682 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

SCGC™ PVC PF741 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG680 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG740 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG770 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

S411B is a high strength polyethylene resin designed for small blow molding containers (size up to 6 L). This grade provides excellent combination of stiffness and chemical resistance for light weight container.

SCGC™ S495B is a high strength polyethylene resin designed to provides excellent combination of stiffness and chemical resistance for blow molding container size upto 20L

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

SCGC™ PP X811T is high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

SCGC™ PP X861T is a high impact polypropylene copolymer designed for automotive compounds. This resin is recommended for product that require high impact strength with good processability.

PCRH01BN is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine. This product is not intended for food contact, pharmaceutical or medical applications.

PCRH02BW is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

PCRH03BB is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH01BN is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH02BW is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDP01JN is a certified Post-Consumer Recycled Resin polypropylene with odorless feature. This grade is suitable for injection molding application using injection molding machine.

AP303S is a circular polypropylene homopolymer resin, the development of advanced recycling technology that turn post consumer plastic into renewable feedstock for virgin plastic resin plastic resin production

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC™ PP P905J is a homopolymer polypropylene resin with high flowability, ultra clarity and good mechanical property balance. It is particularly designed for the thin wall injection moulding of transparent packaging.

SCGC PP P1088J is a high flowability and high crystalline polypropylene impact copolymer which designed for thin wall injection molding.

SCGC PP P341S is an impact copolymer polypropylene with low flowability.

SCGC GREEN POLYMER™ Circular Polypropylene A10P842J is contained 10% recycling content derived from advanced recycling technology that turn post-consumer plastics into recycled feedstock for virgin like plastic production. AP10P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC GREEN POLYMER™ Circular Polypropylene A10P740J is contained 10% recycling content derived from advanced recycling technology that turn post-consumer plastics into recycled feedstock for virgin like plastic production. A10P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC PP, P140S is an impact copolymer polypropylene with very low flowability

SCGC™ PCRLB02P contains 57% post-consumer recycled polyethylene for rotational molding applications. It is available in natural color PCR resin, translucent light brown color, which provided in pellet (PCRLB02) and powder form (PCRLB02P). The product exhibits high melt flow rate and balance of impact strength, stiffness, and processability. It is suitable for furniture, decorative items, and other general purpose articles. The post-consumer recycled resin, PCRLB02, exhibits a carbon footprint of 1.20 kilograms of CO2 equivalent per kilogram of product.

SCGC™ LLDPE M10 series is color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. This grade is suitable for rotational moulding of storage tanks and general purpose applications.

SCGC™ LLDPE M50 series is color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. M50 is specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy. Both of them are recommended for large and thick tanks with a generous radius and curve.

SCGC™ LLDPE M70 series is color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. With a high melt flow and a balance of impact strength, stiffness, and processability, this grade is suitable for rotational moulding of lawn and garden articles, decorative items, and small industrial parts.

SCGC™ LLDPE M90 series is color compound linear-low density polyethylene (LLDPE) for rotational moulding applications. M90 is available in a pellet and powder form. This grade is suitable for rotational moulding of large water tanks and parts that require high stiffness.

SCGC™ PVC PR701 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC PP P1000J is a very high-flowability and high-crystallinity homopolymer polypropylene designed to optimize flow and stiffness performance for automotive compounding applications requiring thin-walled injection molding. It is also suitable as a base resin for fiber-reinforced polypropylene composites.

SCGC™ M1FBKA2P is a black, halogenated, polyethylene (PE)-based compound designed for rotational molding applications. It meets the UL 94 V-2 flame retardancy standard, UL 746A, and includes a UV stabilizer package for long-lasting performance in both indoor and outdoor environments.

SCGC™ M735RWP is the powder form of M735RW, a linear low-density polyethylene (LLDPE) grade designed for rotational moulding applications. Offering high melt flow and an excellent balance of impact strength, stiffness, and processability, this grade is ideal for lawn and garden articles, decorative items, and small industrial parts.

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC GREEN POLYMER™ PCDP02JN is a certified odorless Post-Consumer Recycled Resin impact copolymer polypropylene. This grade is suitable for injection molding application. This product is not intended for food contact, pharmaceutical or medical applications.

SCG GREEN POLYMER™ grade PCDL01FN is a 100% certified Post-Consumer Recycled linear-low density polyethylene resin. This grade is suitable for LLDPE film application. This product is suitable for applied as film packaging and not intended for direct food contact, pharmaceutical or medical applications.

SCGC GREEN POLYMER™ PCRP03JB is a certified Post-Consumer Recycled Resin impact copolymer polypropylene. This grade is suitable for injection molding application. This product is not intended for food contact, pharmaceutical or medical applications.

SCGC™ M50BKM1P is a black compound which is a linear-low density polyethylene octene copolymer for rotational moulding applications. M50BKM1P is specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. It is fully heat and UV stabilized resulting in a wide processing latitude, good color retention, and long life expectancy.

SCGC™ 1507BKAP is a cross-linkable polyethylene powder for rotational molding. Specifically engineered for diesel fuel tanks in truck and agricultural tractor this grade delivers exceptional durability under high-heat conditions, high impact resistance, and excellent ESCR. Available in black.

SCGC Green Polymer^TM