SCGC™ PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

Properties	Test Methods	Value	Unit
Melt Flow Rate at 230 °C and 2.16 kg	ASTM D 1238	28	g/10 min
Izod Impact Strength at 23°C	ASTM D 256	50	J/m
Izod Impact Strength at 0 °C	ASTM D 256	26	J/m
Flexural Modulus	ASTM D 790	12,000	kg/cm²
Haze	ASTM D 1003	< 20	%

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P403J is a homopolymer polypropylene resin suitable for general propose product which required good impact resistance produced from injection molding process.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P441JU is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires good outdoor performance.

SCGC™ PP P483JU is a developmental of high stiffness polypropylene impact copolymer product which contains anti-static agent and UV stabilizer. It is designed for very high stiffness, creep resistance, and high heat resistance while maintain a good impact strength than those of general impact copolymer polypropylene and suitable for injection molding application.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P642J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is suitable for Injection molding process. This resin is recommended for product that requires high impact strength and stiffness.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P700J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process from SCG.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P722JO is polypropylene impact copolymer which contains UV stabilizer. This resin is recommended for producing battery case from injection molding process.

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P840J is a high flow ability impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P841J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires very high processability and good UV performance.

SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC™ PP P851JO is a random copolymer polypropylene resin which giving high clarity, high brightness, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

SCGC™ HDPE H6308JU is a high density polyethylene resin with good processibility and UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE S414B is a high density polyethylene resin produced by SMX™ technology. This grade can be processed at high speed blow molding machine. It is recommended for milk bottles.

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P303S is a homopolymer polypropylene resin with high stiffness and high clarity. It is designed for sheet and solid phase pressure thermoforming products.

SCGC™ PP P348S is a special impact copolymer polypropylene base resin which is suitable for sheet and thermoforming products that required high thermal stability and high impact strength at low temperature. It is particularly designed for solid phase pressure forming.

SCGC™ PP P601F is a homopolymer polypropylene resin for water-quenched blown film.This grade is contain high slip and antiblock agent and recommended for applications that film thickness is lower than 50 micron.

SCGC™ PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. This grade is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

SCGC™ PVC PC750 is a high molecular weight homoploymer paste PVC resin, produced by TPC Paste Co.,Ltd. under OxyChem's HYBRID technology

PF682 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co., Ltd. under OxyChem's HYBRID® Technology.

SCGC™ PVC PF741 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG680 is a medium molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG740 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

SCGC™ PVC PG770 is a high molecular weight homopolymer paste PVC resin, produced by TPC Paste Resin Co.,Ltd. under OxyChem's HYBRID technology

S411B is a high strength polyethylene resin designed for small blow molding containers (size up to 6 L). This grade provides excellent combination of stiffness and chemical resistance for light weight container.

SCGC™ S495B is a high strength polyethylene resin designed to provides excellent combination of stiffness and chemical resistance for blow molding container size upto 30L

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

PCRH02BW is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

PCRH03BB is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH01BN is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDH02BW is a certified Post-Consumer Recycled Resin high density polyethylene with odorless feature. This grade is suitable for blow molding application using extrusion blow molding machine.

PCDP01JN is a certified Post-Consumer Recycled Resin polypropylene with odorless feature. This grade is suitable for injection molding application using injection molding machine.

AP303S is a circular polypropylene homopolymer resin, the development of advanced recycling technology that turn post consumer plastic into renewable feedstock for virgin plastic resin plastic resin production

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

SCGC™ PP P905J is a homopolymer polypropylene resin with high flowability, ultra clarity and good mechanical property balance. It is particularly designed for the thin wall injection moulding of transparent packaging.

SCGC PP P341S is an impact copolymer polypropylene with low flowability.

SCGC™ PP P304S is a homopolymer polypropylene resin with good process ability and good mechanical properties. It is particularly designed for sheeting and thermoforming products required good stiffness stability, toughness property and clarity.

SCGC GREEN POLYMER™ Circular Polypropylene A10P740J is contained 10% recycling content derived from advanced recycling technology that turn post-consumer plastics into recycled feedstock for virgin like plastic production. A10P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC PP, P140S is an impact copolymer polypropylene with very low flowability