SCGC™ HDPE SX002JA is a high density polyethylene resin with superior stress cracking resistant and excellent mechanical property balance. It is particularly designed for light-weight carbornated soft drink caps. This resin has excellent processability for both injection molding and continuous compression molding.

Properties Test Methods Value Unit
Melt Flow Rate at 190 °C and 2.16 kg ISO 1133 0.55 g/10 min
Density ISO 1183-2 0.955 g/cm³
Tensile Modulus (1B, 1mm/min) ISO 527 1,000 MPa
Tensile Strength at Yield (1B, 50 mm/min) ISO 527 25 MPa
Tensile strength at Break (1B, 50 mm/min) ISO 527 16 MPa
Elongation at Yield (1B, 50 mm/min) ISO 527 11 %
Flexural Modulus ISO 178 1,100 MPa
Charpy impact strength at 23 °C ISO 179 8 kJ/m²
Environmental Stress Cracking Resistance (ESCR), F50, conditionB, 10% lgepal ASTM D 1693 > 1,000 hrs
Melting Point ASTM D 2117 130 °C
HDT at 4.6 kg/cm² ASTM D 648 70 °C