SCGC GREEN POLYMER™ SX002J is a high density polyethylene resin with superior stress cracking resistant and excellent mechanical property balance. It is particularly designed for light-weight carbornated soft drink caps. This resin has excellent processability for both injection molding and continuous compression molding.

Properties Test Methods Value Unit
Melt Flow Rate at 190 °C and 2.16 kg ASTM D 1238 0.55 g/10 min
Density ASTM D 1505 0.955 g/cm³
Tensile Modulus ISO 527 1,000 MPa
Tensile Strength at Yield ISO 527 25 MPa
Tensile strength at Break ISO 527 16 MPa
Elongation at Yield ISO 527 11 %
Flexural Modulus ASTM D 790 11,000 kg/cm²
Charpy impact strength at 23 °C ISO 179 8 kJ/m²
Environmental Stress Cracking Resistance (ESCR), F50, conditionB, 10% lgepal ASTM D 1693 > 1,000 hrs
Full Notch Creep Test (FNCT), 50°C, 6MPa, 2%wt Arkopol ISO 16770 55 hrs
Melting Point ASTM D 2117 130 °C
HDT at 4.6 kg/cm² ASTM D 648 70 °C