Description

SCGC™ PP P350F is a copolymer polypropylene without slip and anti-blocking agents for cast film application with excellent seal properties, excellent clarity and good stress whitening resistance.

Properties Test Methods Value Unit
Melt Flow Rate at 230 °C and 2.16 kg ASTM D 1238 3.20 g/10 min
Density ASTM D 1505 0.90 g/cm³
Melting Point ASTM D 2117 161 °C
VICAT Softening Temperature ASTM D 1525 140 °C
Flexural Modulus ASTM D 790 900 kg/cm²
Tensile Strength at Yield ASTM D 1238 @ 190 °C, 2.16 kg MD 20*, TD 20* MPa
Tensile Strength at Break ASTM D 882 MD 39*, TD 25* MPa
Tensile Modulus, 2% Secant ASTM D 882 MD 406*, TD 370* kg/cm²
Elongation at Break ASTM D 882 MD 804*, TD 656* %
US FDA 21 CFR 177.1520 - ✓
Regulation (EU) No.10/2011 - ✓
Japan Chemical Innovation and Inspection Institute (JCII) - ✓
Haze ASTM D 1003 11 %
Seal Strength (Before retort) TPE Method >2 kgf/15mm
Seal Strength (After retort) TPE Method >2 kgf/15mm
DOWNLOADS
Data Sheet
Safety Data Sheet
Brochure

RELATED PRODUCT GRADES

D388C
SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.
D477C
SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.
D777C
SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.
H377C
SCGC™ HDPE H377C is a bi-modal high density polyethylene resin for cast film, extrusion coating and lamination applications. The resin provides excellent film stiffness, temperature resistance and good compatibility with LLDPE and LDPE scratch resistance.
H619F
H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE
L1210F
SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.
L1211FA
SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.
L1220F
SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.
L1221FA
SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.
L1810FI
SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.
L2009F
SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.
L2009FA
SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.
P405F
SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.
P607F
SCGC PP P607F is a homopolymer polypropylene resin without slip and antiblock agent designed for core layer of co-extrusion cast film, monolayer cast film application with high stiffness & clarity, and flat yarn with high tenacity for high speed slit tape machine with balance good mechanical properties for yarn application.
SG66Z
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.
M345C
SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC
P408F
SCGC™ PP P408F is homo polypropylene resin for biaxially oriented polypropylene film. This resin is designed for superior heat resistance and high stiffness which is suitable for mono-material PP packaging.
SB31L
Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in op
SB32L
Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result
PA17L
Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.
P409F
SCGC™ PP P409F is nucleated homopolypropylene resin for BOPP film. This resin offers excellent stiffness and thermal resistance. It suitable for mono-material PP packaging which needed heat resistance such as retort packaging.
S197F
SCGC™ HDPE S197F is a polyethylene designed especially for biaxially oriented film via a tenter frame technology of BOPE film. It offers high heat resistance, stiffness and toughness, being suitable for mono-material PE packaging.
P790C
SCGC™ PP P790C is hetero-polypropylene resin for extrusion coating/lamination application. This resin offers good seal performance and good adhesion on BOPP film. In addition, it provide good neck in and excellent processing at high line speed coating. This grade contains slip.
P791C
SCGC™ PP P791C is a polypropylene product which is specially designed for extrusion coating or lamination with excellent bonding strength for PP substrate, toughness, and impact strength. SCGCTM PP P791C can be used in high performance coating application for example cement bag, high load FIBC bag, and high performance laminated woven bag with BOPP etc.
L1231FA
SCGC LLDPE L1231FA is a butene LLDPE resin without slip and antiblocking agent. It is designed for good process ability with high productivity, high thermal stability, and good optical properties. It is recommended for cast stretch wrap film and genaral packaging
arrow-02-r
arrow-02-l

SCGC Solutions

Flexible Pouch and Bag
Icon Solutions Flexible Pouch And Bag
arrow-02-r
arrow-02-l
dot footer
SCG Chemicals
Public Company Limited
1 Siam Cement Road, Bangsue,
Bangkok 10800 Thailand
icon-phone+662-586-1111
arrow-right-1Contact Us icon searchSubscribe
Follow us :
  • icon-fb
  • icon-tw
  • icon-yt
  • icon-in
  • icon-line

Copyright © SCG Chemicals Public Company Limited (2022). All Rights Reserved.