GRADE

L546WC

SCGC™ LLDPE L546WC is a black linear low density polyethylene compound for jacketing in communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.

Properties	Test Methods	Value	Unit
Density	ASTM D 1505	0.943 (compound)	g/cm³
Melt Flow Rate at 190 °C and 2.16 kg	ASTM D 1238	1.12	g/10 min
Tensile Strength at Break	ASTM D 638 @ Crosshead speed 50 mm/min	29	MPa
Elongation at Break	ASTM D 638 @ Crosshead speed 50 mm/min	> 800	%
ESCR @ 50 °C	ASTM D 1693	> 1,000	hrs, F0, 10% Igepal

RELATED PRODUCT GRADES

SCGC™ HDPE H2001WC is a black bimodal high density polyethylene compound for jacketing in fiber optic and power cable applications. It contains well-dispersed carbon black to provide excellent weathering and UV resistance.

SCGC™ HDPE H512W is a high density polyethylene for solid insulation in cable application. It is also suitable for outer skin in

SCGC™ HDPE H624WC is a black bimodal high density polyethylene compound for jacketing of fiber optic and power cable applications. Its MFR and density are outer the traditional range which provide better processability, and also contains appropriate level of additives and well-dispersed carbon black to ensure excellent weathering resistance

SCGC™ MDPE M545WC is a black medium density polyethylene compound for jacketing in power cable and communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.

SCGC SOLUTIONS