GRADE

M545WC

Description

SCGC™ MDPE M545WC is a black medium density polyethylene compound for jacketing in power cable and communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.

Properties Test Methods Value Unit
Melt Flow Rate at 190 °C and 2.16 kg ASTM D 1238 0.8 g/10 min
Density ASTM D 1505 0.948 (compound) g/cm³
Tensile Strength at Break (50 mm/min) ASTM D 638 31 MPa
Elongation at Break (50 mm/min) ASTM D 638 > 800 %
Flexural Modulus ASTM D 790 510 kg/cm²
Hardness (Shore D) ASTM D 2240 58
Carbon black content ASTM D 4218 2.5 %wt
Carbon black dispersion (Rating) ISO 18553 ≤ 3 Rating
Oxidative induction time at 200°C ASTM D 3895 > 90 min
ESCR @ 50 °C ASTM D 1693 > 1,000 hrs, F0, 10% Igepal
DOWNLOADS
Data Sheet
Safety Data Sheet
Brochure

RELATED PRODUCT GRADES

H1000PC
SCGC™ HDPE H1000PC is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
H1000PCI
SCGC™ HDPE H1000PCI is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. It is particularly designed for injection molding for pipe fittings.In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
H112PC
SCGC™ HDPE H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology. SCGC™ HDPE H112PC is classified as MRS 11.2 material (PE112). It provides superior long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides that, it can be produced in all ranges of pipe diameters, especially recommended for the production of very thick wall and large diameter pipe.
H2001WC
SCGC™ HDPE H2001WC is a black bimodal high-density polyethylene compound for jacketing of fiber optic and power cable applications. It contains appropriate level of additives and well-dispersed carbon black to ensure excellent weathering and UV resistance.
H512W
SCGC™ HDPE H512W is a high density polyethylene for solid insulation in cable application. It is also suitable for outer skin in
H5211PC
SCGC™ HDPE H5211PC is a black, bimodal technology, high density polyethylene compound classified as MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. SCGC™ HDPE H5211PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
H624WC
SCGC™ HDPE H624WC is a black bimodal high-density polyethylene compound for jacketing of fiber optic and power cable applications. Its MFR and density are outer the traditional range which provide better processability, and also contains appropriate level of additives and well-dispersed carbon black to ensure excellent weathering and UV resistance.
L546WC
SCGC™ LLDPE L546WC is a black linear low density polyethylene compound for jacketing in communication cable applications. It contains well-dispersed carbon black to provide excellent weathering resistance and UV resistance.
M3863RW
SCGC™ M3863RW is a linear-low density polyethylene (LLDPE) for rotational moulding with Hexene co-monomer (C6). M3863RW is a natural color PE resin aviailable in a pellet form. With an extra UV resistance (UV20), high stiffness and good impact resistance, long durability and excellent ESCR, this grade suitable for rotational moulding of large water tanks, undergroud tanks and chemical tanks
M9001RW / M90
SCGC™ LLDPE M9001RW is a linear-low density polyethylene (LLDPE) for rotational moulding applications. M9001RW is a natural color available in a pellet and powder form, whereas M90 is the color compound version. This grade is suitable for rotational moulding of large water tanks and parts that require high stiffness.
SG580
Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
SG660
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
SG710
Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
SG71J
Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
SG71Z
Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.
SG840
Polyvinyl Chloride Homopolymer having high molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities properties e.g. high strength, needed in many applications. The high K value PVC resin is developed to serve the application which high mechanical properties e.g. high strength, strength, high pressure are needed.
H1000PCH
SCGC™ HDPE H1000PCH is a black, bimodal technology, high density polyethylene compound. It is classified as a PE100RC material with excellent resistance to crack, following the material requirements of EN1555-1:2021, EN12201-1:2024, ISO4437-1:2024
GG700
DE4214WC
SCGC XLPE Peroxide compound for spaced aerial cable is a black colored, peroxide crosslinkable low density polyethylene compound with well-dispersed carbon black designed for jacketing of spaced aerial cable up to 33 kV.
S999PC
SCGC HDPE S999PC Very High Abrasion Resistance (VHAR) is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, tri-modal technology. It provides superior abrasion resistance which is especially recommended for aggressive slurry media transferring Mining and Dredging application. It has been designed for good long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance together with excellent sagging resistance property.
SC71Z

SCGC Solutions

Building and Infrastructure
Wire and Cable
Underground Application
dot footer
SCG Chemicals
Public Company Limited
1 Siam Cement Road, Bangsue,
Bangkok 10800 Thailand
+662-586-1111
Contact Us Subscribe
Follow us :

Copyright © SCG Chemicals Public Company Limited (2022). All Rights Reserved.