close

GRADE

L1231FA

L1231FA

SCGC™ LLDPE 1231FA is a butene LLDPE resin without slip and antiblocking agent. It is designed for good process ability with high productivity, high thermal stability, and good optical properties. It is recommended for cast stretch wrap film and genaral packaging.

Properties	Test Methods	Value	Unit
Melt Flow Rate at 190 °C and 2.16 kg	ASTM D 1238	2.8	g/10 min
Density	ASTM D 1505	0.920	g/cm³
Melting Point	ASTM D 2117	121	°C

Film Properties
Tensile strength at Break	ASTM D 882	MD: 100, TD:90	kg/cm²
Elongation at Break	ASTM D 882	MD:900, TD:1000	%
Elemendoft Tear Strength	ASTM D 1922	MD: 250, TD:270	g
Dart Drop Impact	ASTM D 1709A	70*	g
Haze	ASTM D 1003	2*	%
Gloss	ASTM D 2457	91*	%

Safety Data Sheet

SDS_SCGC LLDPE (EN)

RELATED PRODUCT GRADES

SCGC™ HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P440J is an impact to co-polypropylene designed for injection molding process. This resin is recommended for product that requires high impact strength with good stiffness.

SCGC™ PP P441JU is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires good outdoor performance.

SCGC™ PP P483JU is a developmental of high stiffness polypropylene impact copolymer product which contains anti-static agent and UV stabilizer. It is designed for very high stiffness, creep resistance, and high heat resistance while maintain a good impact strength than those of general impact copolymer polypropylene and suitable for injection molding application.

SCGC™ PP P640J is an impact to co-polypropylene resin designed for injection molding process. This resin require is recommended for product that requires high impact strength with good stiffness and processiblity.

SCGC™ PP P642J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is suitable for Injection molding process. This resin is recommended for product that requires high impact strength and stiffness.

SCGC™ PP P686J is an impact copolymer polypropylene resin which contains nucleating agent. It is designed for injection molding process. This resin recommended for product that requires high impact strength with high stiffness and good productivity.

SCGC™ PP P722JO is polypropylene impact copolymer which contains UV stabilizer. This resin is recommended for producing battery case from injection molding process.

SCGC™ PP P740J is a medium flow impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P744J is polypropylene impact copolymer designed for high speed injection molding process. This resin is recommended for product that requires high stiffness and high processability.

SCGC™ PP P840J is a high flow ability impact copolymer polypropylene resin designed for injection molding process. This resin is recommended for product that requires good stiffness and impact balance.

SCGC™ PP P841J is polypropylene impact copolymer which contains anti-static agent and UV stabilizer. It is designed for injection molding process. This resin is recommended for product that requires very high processability and good UV performance.

SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE F15 is a high density polyethylene product of bi-modal process. It is recommended for film which is produced by high speed machine and wide lay flat. The key characteristics are high tesile strength and high productivity.

SCGC™ HDPE H377C is a bi-modal high density polyethylene resin for cast film, extrusion coating and lamination applications. The resin provides excellent film stiffness, temperature resistance and good compatibility with LLDPE and LDPE scratch resistance.

SCGC™ HDPE H5480S is a high density polyethylene resin which is recommended for monofilament or flat yarn applications. It is specially designed for extrusion process both with spinneret die and T-die. H5480S offers good balance process ability and mechanical properties such as tenacity and elongation.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P350F is a copolymer polypropylene without slip and anti-blocking agents for cast film application with excellent seal properties, excellent clarity and good stress whitening resistance.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCGC PP P607F is a homopolymer polypropylene resin without slip and antiblock agent designed for core layer of co-extrusion cast film, monolayer cast film application with high stiffness & clarity, and flat yarn with high tenacity for high speed slit tape machine with balance good mechanical properties for yarn application.

S111F is a high strength polyethylene produced by SMX™ technology which superior toughness and stiffness. With excellent toughness and stiffness, it can reduce thickness while maintain product performance. It is recommended for high quality film application such as industrial bag.

S199F is a high strength polyethylene produced by SMX™ technology, resulting in better impact strength with excellent process ability. This grade can be produced various film widths from wider operating condition with balancing between mechanical properties and bubble stability. It is recommended for high quality film application in consumer and industrial segment such as general purpose film.

S411B is a high strength polyethylene resin designed for small blow molding containers (size up to 6 L). This grade provides excellent combination of stiffness and chemical resistance for light weight container.

SCGC™ S495B is a high strength polyethylene resin designed to provides excellent combination of stiffness and chemical resistance for blow molding container size upto 30L

Polyvinyl chloride homopolymer having low molecular weight with high porosity. SF58S is white and free-flowing resin produced by suspension polymerization process. The resin is recommended to use for chlorinated poly vinyl chloride process to produce chlorinated poly vinyl chloride (CPVC). Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resin produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer satisfaction.

PCRH02BW is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.This product is not intended for food contact, pharmaceutical or medical applications.

PCRH03BB is a certified Post-Consumer Recycled Resin high density polyethylene. This grade is suitable for blow molding application using extrusion blow molding machine.

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ PP P408F is homo polypropylene resin for biaxially oriented polypropylene film. This resin is designed for superior heat resistance and high stiffness which is suitable for mono-material PP packaging.

Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in op

Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result

Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.

SCGC™ PP P409F is nucleated homopolypropylene resin for BOPP film. This resin offers excellent stiffness and thermal resistance. It suitable for mono-material PP packaging which needed heat resistance such as retort packaging.

SCGC™ HDPE S197F is a polyethylene designed especially for biaxially oriented film via a tenter frame technology of BOPE film. It offers high heat resistance, stiffness and toughness, being suitable for mono-material PE packaging.

SCGC HDPE X84H001B is an extra high molecular weight high density polyethylene resin produced by SMX technology for producing chemical and food containers 20-30 litres by blow molding process. This grade provides excellent chemical resistance with good processability.

SCGC™ PP P790C is hetero-polypropylene resin for extrusion coating/lamination application. This resin offers good seal performance and good adhesion on BOPP film. In addition, it provide good neck in and excellent processing at high line speed coating. This grade contains slip.

SCGC™ PP P791C is a polypropylene product which is specially designed for extrusion coating or lamination with excellent bonding strength for PP substrate, toughness, and impact strength. SCGCTM PP P791C can be used in high performance coating application for example cement bag, high load FIBC bag, and high performance laminated woven bag with BOPP etc.