SCGC™ PP P791C is a polypropylene product which is specially designed for extrusion coating or lamination with excellent bonding strength for PP substrate, toughness, and impact strength. SCGCTM PP P791C can be used in high performance coating application for example cement bag, high load FIBC bag, and high performance laminated woven bag with BOPP etc.

Properties	Test Methods	Value	Unit
Melt Flow Rate at 230 °C and 2.16 kg	ASTM D 1238	22	g/10 min
Density	ASTM D 1505	0.910	g/cm³
Melting Point	ASTM D 2117	148	°C
VICAT Softening Temperature	ASTM D 1525	125	°C
Tensile Strength at Yield	ASTM D 638	208	kg/cm²
Tensile Strength at Break	ASTM D 638	136	kg/cm²
Elongation at Break	ASTM D 638	444	%
Flexural Modulus	ASTM D 790	7,885	kg/cm²

RELATED PRODUCT GRADES

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P403J is a homopolymer polypropylene resin suitable for general propose product which required good impact resistance produced from injection molding process.

SCGC™ PP P700J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process from SCG.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE H377C is a bi-modal high density polyethylene resin for cast film, extrusion coating and lamination applications. The resin provides excellent film stiffness, temperature resistance and good compatibility with LLDPE and LDPE scratch resistance.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE

SCGC™ HDPE S414B is a high density polyethylene resin produced by SMX™ technology. This grade can be processed at high speed blow molding machine. It is recommended for milk bottles.

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P303S is a homopolymer polypropylene resin with high stiffness and high clarity. It is designed for sheet and solid phase pressure thermoforming products.

SCGC™ PP P348S is a special impact copolymer polypropylene base resin which is suitable for sheet and thermoforming products that required high thermal stability and high impact strength at low temperature. It is particularly designed for solid phase pressure forming.

SCGC™ PP P350F is a copolymer polypropylene without slip and anti-blocking agents for cast film application with excellent seal properties, excellent clarity and good stress whitening resistance.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCGC™ PP P601F is a homopolymer polypropylene resin for water-quenched blown film.This grade is contain high slip and antiblock agent and recommended for applications that film thickness is lower than 50 micron.

SCGC™ PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. This grade is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

SCGC PP P607F is a homopolymer polypropylene resin without slip and antiblock agent designed for core layer of co-extrusion cast film, monolayer cast film application with high stiffness & clarity, and flat yarn with high tenacity for high speed slit tape machine with balance good mechanical properties for yarn application.

S411B is a high strength polyethylene resin designed for small blow molding containers (size up to 6 L). This grade provides excellent combination of stiffness and chemical resistance for light weight container.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

AP303S is a circular polypropylene homopolymer resin, the development of advanced recycling technology that turn post consumer plastic into renewable feedstock for virgin plastic resin plastic resin production

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ PP P408F is homo polypropylene resin for biaxially oriented polypropylene film. This resin is designed for superior heat resistance and high stiffness which is suitable for mono-material PP packaging.

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in op

Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result

Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.

SCGC™ PP P905J is a homopolymer polypropylene resin with high flowability, ultra clarity and good mechanical property balance. It is particularly designed for the thin wall injection moulding of transparent packaging.

SCGC PP P341S is an impact copolymer polypropylene with low flowability.

SCGC™ PP P304S is a homopolymer polypropylene resin with good process ability and good mechanical properties. It is particularly designed for sheeting and thermoforming products required good stiffness stability, toughness property and clarity.

SCGC™ PP P409F is nucleated homopolypropylene resin for BOPP film. This resin offers excellent stiffness and thermal resistance. It suitable for mono-material PP packaging which needed heat resistance such as retort packaging.

SCGC™ HDPE S197F is a polyethylene designed especially for biaxially oriented film via a tenter frame technology of BOPE film. It offers high heat resistance, stiffness and toughness, being suitable for mono-material PE packaging.

SCGC™ PP P790C is hetero-polypropylene resin for extrusion coating/lamination application. This resin offers good seal performance and good adhesion on BOPP film. In addition, it provide good neck in and excellent processing at high line speed coating. This grade contains slip.

SCGC Solutions

Flexible Pouch and Bag

Food and Beverage Container