| Melt Flow Rate at 190 °C and 2.16 kg |
ISO 1133 |
0.8 |
g/10 min |
| Density |
ISO 1183-2 |
0.955 |
g/cm³ |
| Tensile Modulus (1B, 1mm/min) |
ISO 527 |
1,100 |
MPa |
| Tensile Strength at Yield (1B, 50 mm/min) |
ISO 527 |
25 |
MPa |
| Tensile strength at Break (1B, 50 mm/min) |
ISO 527 |
15 |
MPa |
| Elongation at Yield (1B, 50 mm/min) |
ISO 527 |
10 |
% |
| Flexural Modulus |
ISO 178 |
1,250 |
MPa |
| Charpy impact strength at 23 °C |
ISO 179 |
7 |
kJ/m² |
| Environmental Stress Cracking Resistance (ESCR), F50, conditionB, 10% lgepal |
ASTM D 1693 |
>600 |
hrs |
| Melting Point |
ASTM D 2117 |
130 |
°C |
| HDT at 4.6 kg/cm² |
ASTM D 648 |
70 |
°C |