General Packaging

Total 12 grades

SCG Chemicals polyolefin-based resin is increasingly used by converters for production of general packaging which requires high performance, quality and consistency.

General purpose packaging using our Mitsui-technology polyolefin enables converters to produce packaging film with high tensile strength, a good moisture barrier, excellent stiffness, and excellent optical properties – as cost effectively as possible.

Show products by

HDPE (5)

Density (g/cm³)

ESCR @ 50 °C (hrs, F50)

Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)

Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)

H5604F

0.954

> 1000

Description

SCG HDPE H5604F is a high density polyethylene product of bi-modal process which suitable for the high quality film application. It is recommended for general purpose film with high tensile strength H5604F is a high density polyethylene product of bi-modal process which suitable for the high quality film application. It is recommended for general purpose film with high tensile strength H5604F is a high density polyethylene product of bi-modal process which suitable for the high quality film application. It is recommended for general purpose film with high tensile strength.

Related Finished Products

Shopping bag and T-shirt bag, garbage bag, liner bag

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.954
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	131
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.04
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 620, TD 310
VICAT Softening Temperature (°C)	ASTM D 1525	124

Download

SDS

TDS

General Plastics

H5840B

0.955

300

Description

SCG HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

Related Finished Products

Chemical bottles, Chemical drums, (Containing volume up to 30 liters), Personal and homecare bottles, Lube oil bottles, Brake fluid bottles

Properties	Test Methods	Value
Density	ASTM D 792
Density (g/cm³)	ASTM D 1505	0.955
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	300
Flexural Modulus (kg/cm²)	ASTM D 790	12,000
IZOD 23 °C (J/m)	ASTM D 256	98
Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)	ASTM D 1238
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.4
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	280
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6140B

0.96

100

Description

SCG HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

Related Finished Products

Personal and homecare bottles, Lube oil bottles, Brake fluid bottles, Chemical bottles, Milk bottles

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.96
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	100
Flexural Modulus (kg/cm²)	ASTM D 790	13000
IZOD 23 °C (J/m)	ASTM D 256	98
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.3
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	300
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6430BM

0.964

Description

SCG HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

Related Finished Products

Drinking water bottles (containing volume up to 20 liter), milk bottles, fruit juice bottles, fish sauce gallons

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.964
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	24
Flexural Modulus (kg/cm²)	ASTM D 790	15000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.4
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	300
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6670B

0.965

Description

SCG HDPE H6670B is a high density polyethylene resin suitable for producing milk bottles by using extrusion blow molding machine

Related Finished Products

Milk bottles, fruit juice bottles.

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.965
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	24
Flexural Modulus (kg/cm²)	ASTM D 790	15000
IZOD 23 °C (J/m)	ASTM D 256	147
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.7
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	320
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

LLDPE (3)

Density (g/cm³)

Flexural Modulus (MPa)

Melt Index at 190 °C and 2.16 kg (g/10 min)

VICAT Softening Temperature (°C)

L1810FI

0.921

1.00

102

Description

SCG LLDPE L1810FI is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for water-quenched blown film for vegetable or fruit packaging with high clarity and good openability.

Related Finished Products

Heavy duty bag, industrial bag, fruit & vegetable bag, water-quench blown film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.921
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Melting Point (°C)	ASTM D 2117	122
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 470, TD 170
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

L2009F

0.921

1.00

102

Description

SCG LLDPE L2009F is a butene linear resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

Related Finished Products

Heavy duty bag, industrial bag, agricultural film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.921
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 380, TD 350
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

L2009FA

0.92

1.00

102

Description

SCG LLDPE L2009FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

Related Finished Products

Heavy duty bag, industrial bag, agricultural film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.92
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Melting Point (°C)	ASTM D 2117	122
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 380, TD 350
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

PP Homopolymer (3)

Flexural Modulus (kg/cm²)

IZOD 23 °C (J/m)

Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)

Melting Point (°C)

P600F

17000

160

Description

P600F is a homopolymer polypropylene resin with slip and antiblock agent. It is recommended for water-quenched blown film for food and clothe pakaging with good optical porperties and high productivity.

Related Finished Products

Food packaging

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.91
Flexural Modulus (kg/cm²)	ASTM D 790	17000
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	10
Melt FlowRate at 230 °C and 2.16 kg	ASTM D 1238	10
Melting Point (°C)	ASTM D 2117	160
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 280, TD 260
VICAT Softening Temperature (°C)	ASTM D 1525	155

Download

SDS

TDS

General Plastics

P600FS

14500

Description

SCG™ PP P600FS is a homopolymer polypropylene resin which provides excellent openability and excellent optical.

Related Finished Products

Water-quenched blown film for thin packaging (<20 micron)

Properties	Test Methods	Value
Elongation at break (%)	ASTM D 638 @ Crosshead speed 50 mm/min	MD 450, TD 30
Flexural Modulus (kg/cm²)	ASTM D 790	14500
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	12
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 220, TD 80

Download

SDS

General Plastics

P602F

17000

160

Description

SCG PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. It is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

Related Finished Products

Food packaging, Display bag such as garment or souvenir etc. (> 100 micron)

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.91
Flexural Modulus (kg/cm²)	ASTM D 790	17000
IZOD 23 °C (J/m)	ASTM D 256
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	10
Melt FlowRate at 230 °C and 2.16 kg	ASTM D 1238	10
Melting Point (°C)	ASTM D 2117	160
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 270, TD 100
VICAT Softening Temperature (°C)	ASTM D 1525	155

Download

SDS

TDS

General Plastics

SMX™ Technology (1)

Density (g/cm³)

ESCR @ 50 °C (hrs, F50)

Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)

Melting Point (°C)

S111F

0.945

0.04

128

Description

S111F is a high density polyethylene product by unique technology which superior toughness and stiffness. This grade can be processed at high output blown film extrusion with excellent bubble stability. It is recommended for high quality film application such as industrial bag and products for property modification.

Related Finished Products

Poultry bag
Industrial liner
Ice bag
Box liner
Premium shopping bag
Trash bag

Properties	Test Methods	Value
Dart Impact Strength(g)	ASTM D 1709	>300
Density	ASTM D 792
Density (g/cm³)	ASTM D 1505	0.945
ESCR @ 50 °C (hrs, F50)	ASTM D 1693
Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)	ASTM D 1238	0.04
Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)	ASTM D 1238
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.04
Melting Point (°C)	ASTM D 2117	128

Download

SDS

TDS

General Packaging

Total 12 grades

SCG Chemicals polyolefin-based resin is increasingly used by converters for production of general packaging which requires high performance, quality and consistency.

Show products by

HDPE (5)

Density (g/cm³)

ESCR @ 50 °C (hrs, F50)

Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)

Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)

H5604F

0.954

> 1000

Description

Related Finished Products

Shopping bag and T-shirt bag, garbage bag, liner bag

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.954
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	131
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.04
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 620, TD 310
VICAT Softening Temperature (°C)	ASTM D 1525	124

Download

SDS

TDS

General Plastics

H5840B

0.955

300

Description

SCG HDPE H5840B is a high density polyethylene resin suitable for producing chemical bottles by using extrusion blow molding machine

Related Finished Products

Chemical bottles, Chemical drums, (Containing volume up to 30 liters), Personal and homecare bottles, Lube oil bottles, Brake fluid bottles

Properties	Test Methods	Value
Density	ASTM D 792
Density (g/cm³)	ASTM D 1505	0.955
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	300
Flexural Modulus (kg/cm²)	ASTM D 790	12,000
IZOD 23 °C (J/m)	ASTM D 256	98
Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)	ASTM D 1238
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.4
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	280
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6140B

0.96

100

Description

SCG HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

Related Finished Products

Personal and homecare bottles, Lube oil bottles, Brake fluid bottles, Chemical bottles, Milk bottles

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.96
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	100
Flexural Modulus (kg/cm²)	ASTM D 790	13000
IZOD 23 °C (J/m)	ASTM D 256	98
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.3
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	300
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6430BM

0.964

Description

SCG HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

Related Finished Products

Drinking water bottles (containing volume up to 20 liter), milk bottles, fruit juice bottles, fish sauce gallons

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.964
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	24
Flexural Modulus (kg/cm²)	ASTM D 790	15000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.4
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	300
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

H6670B

0.965

Description

SCG HDPE H6670B is a high density polyethylene resin suitable for producing milk bottles by using extrusion blow molding machine

Related Finished Products

Milk bottles, fruit juice bottles.

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.965
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	24
Flexural Modulus (kg/cm²)	ASTM D 790	15000
IZOD 23 °C (J/m)	ASTM D 256	147
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.7
Melting Point (°C)	ASTM D 2117	132
Tensile Strength at Yield (kg/cm²)	ASTM D 638 @ Crosshead speed 50 mm/min	320
VICAT Softening Temperature (°C)	ASTM D 1525	128

Download

SDS

TDS

General Plastics

LLDPE (3)

Density (g/cm³)

Flexural Modulus (MPa)

Melt Index at 190 °C and 2.16 kg (g/10 min)

VICAT Softening Temperature (°C)

L1810FI

0.921

1.00

102

Description

SCG LLDPE L1810FI is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for water-quenched blown film for vegetable or fruit packaging with high clarity and good openability.

Related Finished Products

Heavy duty bag, industrial bag, fruit & vegetable bag, water-quench blown film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.921
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Melting Point (°C)	ASTM D 2117	122
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 470, TD 170
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

L2009F

0.921

1.00

102

Description

Related Finished Products

Heavy duty bag, industrial bag, agricultural film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.921
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 380, TD 350
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

L2009FA

0.92

1.00

102

Description

Related Finished Products

Heavy duty bag, industrial bag, agricultural film

Properties	Test Methods	Value
Dart Drop	-	130
Density (g/cm³)	ASTM D 1505	0.92
ESCR @ 50 °C (hrs, F50)	ASTM D 1693	> 1000
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	1.00
Melting Point (°C)	ASTM D 2117	122
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 380, TD 350
VICAT Softening Temperature (°C)	ASTM D 1525	102

Download

SDS

TDS

General Plastics

PP Homopolymer (3)

Flexural Modulus (kg/cm²)

IZOD 23 °C (J/m)

Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)

Melting Point (°C)

P600F

17000

160

Description

Related Finished Products

Food packaging

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.91
Flexural Modulus (kg/cm²)	ASTM D 790	17000
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	10
Melt FlowRate at 230 °C and 2.16 kg	ASTM D 1238	10
Melting Point (°C)	ASTM D 2117	160
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 280, TD 260
VICAT Softening Temperature (°C)	ASTM D 1525	155

Download

SDS

TDS

General Plastics

P600FS

14500

Description

SCG™ PP P600FS is a homopolymer polypropylene resin which provides excellent openability and excellent optical.

Related Finished Products

Water-quenched blown film for thin packaging (<20 micron)

Properties	Test Methods	Value
Elongation at break (%)	ASTM D 638 @ Crosshead speed 50 mm/min	MD 450, TD 30
Flexural Modulus (kg/cm²)	ASTM D 790	14500
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	12
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 220, TD 80

Download

SDS

General Plastics

P602F

17000

160

Description

Related Finished Products

Food packaging, Display bag such as garment or souvenir etc. (> 100 micron)

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.91
Flexural Modulus (kg/cm²)	ASTM D 790	17000
IZOD 23 °C (J/m)	ASTM D 256
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D1238	10
Melt FlowRate at 230 °C and 2.16 kg	ASTM D 1238	10
Melting Point (°C)	ASTM D 2117	160
Tensile strength at Break (kg/cm²)	ASTM D 882	MD 270, TD 100
VICAT Softening Temperature (°C)	ASTM D 1525	155

Download

SDS

TDS

General Plastics

SMX™ Technology (1)

Density (g/cm³)

ESCR @ 50 °C (hrs, F50)

Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)

Melting Point (°C)

S111F

0.945

0.04

128

Description

Related Finished Products

Poultry bag
Industrial liner
Ice bag
Box liner
Premium shopping bag
Trash bag

Properties	Test Methods	Value
Dart Impact Strength(g)	ASTM D 1709	>300
Density	ASTM D 792
Density (g/cm³)	ASTM D 1505	0.945
ESCR @ 50 °C (hrs, F50)	ASTM D 1693
Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min)	ASTM D 1238	0.04
Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min)	ASTM D 1238
Melt Index at 190 °C and 2.16 kg (g/10 min)	ASTM D1238	0.04
Melting Point (°C)	ASTM D 2117	128

Download

SDS

TDS

General Packaging