The Flexible Packaging Team at Chemicals Business, SCG has a clear mission to be not only your high-quality resin supplier but also your supportive working partner. We are strongly committed to providing customers with the best solution for cost-effective processing, using our high manufacturing technology and a diverse range of products to fulfill customer expectations and requirements.
Our innovative products are:
PE resin for extrusion coating: With superior processability compatible with a wide range of machine speeds, the product possesses excellent drawdown ability and stable thickness control, as well as good organoleptic and neck-in properties.
PE resin for blown film: Enhanced stiffness with a good moisture barrier, an ideal choice for film downguaging.
PE and PP resins for cast film: Enhance stiffness for PE and PP cast film.
| Bio Compostable (1) | Density (g/cm3) - ASTM D 792 | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | ||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| BIOC01FN | 1.33 | 2 | - | - | ||||||||||||||||||||||||
|
Description
SCG Green Polymer grade BIOC01FN is a Bio-Compostable Compound Resin designed for blown film extrusion products. This grade is suitable for various compostable film products. Product Features: Related Finished Products
|
||||||||||||||||||||||||||||
| HDPE (2) | Density (g/cm3) | ESCR @ 50 °C (hrs, F50) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min) | ||||||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| H377C | 0.961 | - | 7.5 | - | ||||||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG HDPE H377C is a bi-modal high density polyethylene resin for flim casting and extrusion lamination to enchance film stiffness. It also provide good compatibility when blended with LLDPE and LDPE or co extruded with LLDPE and LDPE. Related Finished Products
Extrusion coating, lamination or casting for various packaging (for blending with LDPE and LLDPE)
Download
|
||||||||||||||||||||||||||||||||||||||||||||||||||||
| H619F | 0.962 | - | 0.7 | - | ||||||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG HDPE H619F isa high stiffness HDPE desighed to improve film stiffness and barrier properties when co-extruded with LLPE and LDPE. Related Finished Products
Thin film that require high stiffness, and laminated film and tube for food packaging and consumer products
Download
|
||||||||||||||||||||||||||||||||||||||||||||||||||||
| LDPE (3) | Density (g/cm3) | Melt Index at 190 °C and 2.16 kg (g/10 min) | Melting Point (°C) | Neck -in 315 °C (Constant output 50 rpm) (cm) | ||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| D388C | 0.919 | 8 | 107 | 15 | ||||||||||||||||||||||||
|
Description
SCG LDPE D388C is an autoclave low density polyethylene grade for extrusion coating/lamination with good processability and good organoleptic. Related Finished Products
-
Download
|
||||||||||||||||||||||||||||
| D477C | 0.924 | 4 | 112 | 6 | ||||||||||||||||||||||||
|
Description
SCG LDPE D477C is an autoclave low density polyethylene grade for extrusion coating/lamination with good stiffness and neck in performance. Related Finished Products
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
Download
|
||||||||||||||||||||||||||||
| D777C | 0.92 | 7 | 107 | 5 | ||||||||||||||||||||||||
|
Description
SCG LDPE D777C is an autoclave low density polyethylene grade for extrusion coating/lamination with excellent processability and good organoleptic. Related Finished Products
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
Download
|
||||||||||||||||||||||||||||
| PP Copolymer (1) | Flexural Modulus (kg/cm2) | IZOD 23 °C (J/m) | Melt Flow Rate at 230 °C and 2.16 kg (g/10 min) | Melting Point (°C) | ||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P350F | - | 3.2 | 161 | |||||||||||||||||||||||||||||||||||||
|
Description
SCG PP P350F is a polypropylene copolymer without slip and anti-blocking agent designed suitable for cast film process with good seal properties, excellent clarity and good stress whitening resistance. Related Finished Products
• CPP retort film and general CPP film
Download
|
||||||||||||||||||||||||||||||||||||||||
| PP Homopolymer (1) | Flexural Modulus (kg/cm2) | IZOD 23 °C (J/m) | Melt Flow Rate at 230 °C and 2.16 kg (g/10 min) | Melting Point (°C) | |||||||||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P607F | 7 | 162 | |||||||||||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG PP P607F is homopolymer resin without slip and antiblock agent, and suitable for cast film application as a core layer of co-extrusion film or monolayer film requiring high film stiffness and high clarity Related Finished Products
Monolayer cast film, core layer for co-extrusion cast film, metallized film
Download
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||
| SMX™ Technology (1) | Density (g/cm3) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) (ISO 1133) | Melting Point (°C) | ||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| S111F | 0.945 | 0.04 | 128 | |||||||||||||||||||||||||||||||
|
Description
S111F is a high strength polyethylene produced by SMXTM technology which superior toughness and stiffness. This grade can be processed at high output blown film extrusion with excellent bubble stability. It is recommended for high quality film application such as industrial bag and products for property modification. Product characteristics
Related Finished Products
Download
|
||||||||||||||||||||||||||||||||||
The Flexible Packaging Team at Chemicals Business, SCG has a clear mission to be not only your high-quality resin supplier but also your supportive working partner. We are strongly committed to providing customers with the best solution for cost-effective processing, using our high manufacturing technology and a diverse range of products to fulfill customer expectations and requirements.
Our innovative products are:
PE resin for extrusion coating: With superior processability compatible with a wide range of machine speeds, the product possesses excellent drawdown ability and stable thickness control, as well as good organoleptic and neck-in properties.
PE resin for blown film: Enhanced stiffness with a good moisture barrier, an ideal choice for film downguaging.
PE and PP resins for cast film: Enhance stiffness for PE and PP cast film.
| Bio Compostable (1) | Density (g/cm3) - ASTM D 792 | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | |||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| BIOC01FN | 1.33 | 2 | - | - | |||||||||||||||||||||
|
Description
SCG Green Polymer grade BIOC01FN is a Bio-Compostable Compound Resin designed for blown film extrusion products. This grade is suitable for various compostable film products. Product Features: Related Finished Products
|
|||||||||||||||||||||||||
| HDPE (2) | Density (g/cm3) | ESCR @ 50 °C (hrs, F50) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | Melt Flow Rate at 190 °C and 5.0 kg. (g/10 min) | |||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| H377C | 0.961 | - | 7.5 | - | |||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG HDPE H377C is a bi-modal high density polyethylene resin for flim casting and extrusion lamination to enchance film stiffness. It also provide good compatibility when blended with LLDPE and LDPE or co extruded with LLDPE and LDPE. Related Finished Products
Extrusion coating, lamination or casting for various packaging (for blending with LDPE and LLDPE)
Download
|
|||||||||||||||||||||||||||||||||||||||||||||||||
| H619F | 0.962 | - | 0.7 | - | |||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG HDPE H619F isa high stiffness HDPE desighed to improve film stiffness and barrier properties when co-extruded with LLPE and LDPE. Related Finished Products
Thin film that require high stiffness, and laminated film and tube for food packaging and consumer products
Download
|
|||||||||||||||||||||||||||||||||||||||||||||||||
| LDPE (3) | Density (g/cm3) | Melt Index at 190 °C and 2.16 kg (g/10 min) | Melting Point (°C) | Neck -in 315 °C (Constant output 50 rpm) (cm) | |||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| D388C | 0.919 | 8 | 107 | 15 | |||||||||||||||||||||
|
Description
SCG LDPE D388C is an autoclave low density polyethylene grade for extrusion coating/lamination with good processability and good organoleptic. Related Finished Products
-
Download
|
|||||||||||||||||||||||||
| D477C | 0.924 | 4 | 112 | 6 | |||||||||||||||||||||
|
Description
SCG LDPE D477C is an autoclave low density polyethylene grade for extrusion coating/lamination with good stiffness and neck in performance. Related Finished Products
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
Download
|
|||||||||||||||||||||||||
| D777C | 0.92 | 7 | 107 | 5 | |||||||||||||||||||||
|
Description
SCG LDPE D777C is an autoclave low density polyethylene grade for extrusion coating/lamination with excellent processability and good organoleptic. Related Finished Products
Coating/ lamination on various substrates such as plastic film, aluminium foil, cardboard, woven sheet for flexible packaging, release liners, woven sack, industrial wrapping, folding carton
Download
|
|||||||||||||||||||||||||
| PP Copolymer (1) | Flexural Modulus (kg/cm2) | IZOD 23 °C (J/m) | Melt Flow Rate at 230 °C and 2.16 kg (g/10 min) | Melting Point (°C) | |||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P350F | - | 3.2 | 161 | ||||||||||||||||||||||||||||||||||
|
Description
SCG PP P350F is a polypropylene copolymer without slip and anti-blocking agent designed suitable for cast film process with good seal properties, excellent clarity and good stress whitening resistance. Related Finished Products
• CPP retort film and general CPP film
Download
|
|||||||||||||||||||||||||||||||||||||
| PP Homopolymer (1) | Flexural Modulus (kg/cm2) | IZOD 23 °C (J/m) | Melt Flow Rate at 230 °C and 2.16 kg (g/10 min) | Melting Point (°C) | ||||||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P607F | 7 | 162 | ||||||||||||||||||||||||||||||||||||||||||||||||||
|
Description
SCG PP P607F is homopolymer resin without slip and antiblock agent, and suitable for cast film application as a core layer of co-extrusion film or monolayer film requiring high film stiffness and high clarity Related Finished Products
Monolayer cast film, core layer for co-extrusion cast film, metallized film
Download
|
||||||||||||||||||||||||||||||||||||||||||||||||||||
| SMX™ Technology (1) | Density (g/cm3) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) | Melt Flow Rate at 190 °C and 2.16 kg. (g/10 min) (ISO 1133) | Melting Point (°C) | |||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| S111F | 0.945 | 0.04 | 128 | ||||||||||||||||||||||||||||
|
Description
S111F is a high strength polyethylene produced by SMXTM technology which superior toughness and stiffness. This grade can be processed at high output blown film extrusion with excellent bubble stability. It is recommended for high quality film application such as industrial bag and products for property modification. Product characteristics
Related Finished Products
Download
|
|||||||||||||||||||||||||||||||