SCGC™ HDPE S1000P is a natural, tri-modal, high density polyethylene resin designed as a general base resin of color compound for pipe extrusion and stripe.

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.949
Melt Flow Rate at 190 °C and 5.0 kg (g/10 min)	ASTM D 1238	0.19
Melt Flow Rate at 190 °C and 21.6 kg (g/10 min)	ASTM D 1238	6.25
Tensile Strength at Yield (MPa)	ASTM D 638 @ Crosshead speed 50 mm/min	23
Tensile Strength at Yield (MPa)	ISO 527	23
Tensile strength at Break (MPa)	ISO 527	> 30
Elongation at Break (%)	ISO 527	> 600
ESCR 10% Igepal, F0 (hrs)	ASTM D 1693	10,000
Oxidative induction time at 200°C (min)	ISO 11357	> 30

RELATED PRODUCT GRADES

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC™ LLDPE D682PC is a black linear low density polyethylene compound. Well dispersed carbon black creates outstanding UV resistance and thermal stability.

SCGC™ HDPE H1000PBL is a blue (no lighter than RAL 5005), bimodal, high density polyethylene compound that is specially designed for water pressure pipe, especially for drinking water pipe. SCGC™ HDPE H1000PBL is designed as PE100 pipe providing excellent in mechanical properties, and processablitiy. Well dispersed UV stabilizer and anti-oxidant which also provide outstanding UV resistance and high thermal stability for long term using.

SCGC™ HDPE H1000PC is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PCI is a black, bimodal technology, high density polyethylene compound classified as MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. It is particularly designed for injection molding for pipe fittings.In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

SCGC™ HDPE H1000PWI is a white HDPE compound made for external coating on SCGC™ HDPE H1000PC for above ground pipe applications. It provides high mechanical properties, good processability, and low heat absorption. In addition the good dispersion and high concentration of stabilizers contribute excellent long term UV resistance and thermal stability.

SCGC™ HDPE H112PC is a black high density polyethylene compound producing from high selective catalyst in the precise process control system, bimodal technology. SCGC™ HDPE H112PC is classified as MRS 11.2 material (PE112). It provides superior long-term hydrostatic strength balancing with high slow crack growth and rapid crack propagation resistance. It has been designed for better safety factor in long-term use. Besides that, it can be produced in all ranges of pipe diameters, especially recommended for the production of very thick wall and large diameter pipe.

SCGC™ HDPE H5211PC is a black, bimodal technology, high density polyethylene compound classified as MRS 8.0 material (PE80) providing superior in mechanical properties and processablity. SCGC™ HDPE H5211PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, it includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions

Polyvinyl chloride homopolymer having low molecular weight with high porosity. SF58S is white and free-flowing resins produced by suspension polymerization process. The resin is recommended to use for chlorinated poly vinyl chloride process to produce chlorinated poly vinyl chloride (CPVC). Applications are ranging from general purpose to special products regarding customer’s satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

Polyvinyl Chloride Homopolymer having medium molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC™ HDPE H1000PCH is a black, bimodal technology, high density polyethylene compound. It is classified as a PE100RC material with excellent resistance to crack, following the material requirements of EN1555-1:2021.

SCGC SOLUTIONS