close

GRADE

P350F

SCGC™ PP P350F is a copolymer polypropylene without slip and anti-blocking agents for cast film application with excellent seal properties, excellent clarity and good stress whitening resistance.

Retort packaging

Properties	Test Methods	Value
Density (g/cm³)	ASTM D 1505	0.90
Melt Flow Rate at 230 °C and 2.16 kg (g/10 min)	ASTM D 1238	3.20
Tensile Strength at Break (MPa)	ASTM D 882	MD 39, TD 25
Elongation at Break (%)	ASTM D 882	MD 804, TD 656
Haze (%)	ASTM D 1003	11
US FDA 21 CFR 177.1520	-	✓
Regulation (EU) No.10/2011	-	✓

RELATED PRODUCT GRADES

SCGC GREEN POLYMER™ BWO1501G is a water-based barrier coating agent, providing a tailor-made oxygen barrier level with achievable Oxygen Transmission Rate (OTR) of less than 1 cc/m2*day and good adhesion for various plastic substrates

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE H377C is a bi-modal high density polyethylene resin for cast film, extrusion coating and lamination applications. The resin provides excellent film stiffness, temperature resistance and scratch resistance.

SCGC™ HDPE H619F is a high stiffness high density polyethylene resin for co-extrude blown film and machine direction oriented film applications. The resin is designed to offer good moisture barrier performance, high temperature resistance and high film stiffness when blend with LDPE and LLDPE

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P405F is crystal clear single structure homopolymer polypropylene resin for biaxial oriented film application. This resin offers good strechability and high clarity for printing film of flexible packaging.

SCGC™ PP P607F is a homopolymer polypropylene resin without slip and antiblock agents for a core layer of co-extrusion cast film or monolayer cast film applications. It offers high film stiffness, good clarity and processability.

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ GREEN POLYMER S197F

SCGC™ GREEN POLYMER P408F is homo polypropylene resin for biaxially oriented polypropylene film. This resin is designed for superior heat resistance and higher stiffness which is suitable for full PP packaging.

Active Plus™ SB31L is a Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It has an optimal ratio between Slip agent and Antiblock agent. The synergized effect from both substances results in a significant improvement in op

Active Plus™ SB32L is a highly concentrated Slip & Antiblock masterbatch which specifically designed to use with Polyolefins. It provides an optimal mix between Slip agent and Antiblock agent, achieving a synergized effect from both substances. The result

Active Plus™ PA17L is a fluorinated processing aids masterbatch which design to use with polyolefin based polymer and also effective for many other applications which require a smoothen surface.

SCGC SOLUTIONS

Flexible Pouch and Bag