GRADE

H6308JU

SCGC™ HDPE H6308JU is a high density polyethylene resin with good processibility and UV resistance suitable for industrial product produced from injection molding process.

Properties	Test Methods	Value	Unit
Density	ASTM D 1505	0.963	g/cm³
Melt Flow Rate at 190 °C and 2.16 kg	ASTM D 1238	8.20	g/10 min
Tensile Strength at Yield	ASTM D 638 @ Crosshead speed 50 mm/min	310	kg/cm²
Flexural Modulus	ASTM D 790	13,500	kg/cm²
Notched Izod Impact Strength at 23°C	ASTM D 256	3.5	Kg.cm/cm

RELATED PRODUCT GRADES

SCGC™ HDPE H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using extrusion blow molding machine

SCGC™ PP P400S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P400S offers good features for Flat Yarn application as consistency process ability, high productivity with balance good mechanical properties.

SCGC™ PP P401S is a homopolymer polypropylene resin which is specially designed for flat yarn or raffia products and monofilament application as well. P401S offers good features for Flat Yarn application as consistency process ability and high mechanical properties.

SCGC™ PP P403J is a homopolymer polypropylene resin suitable for general propose product which required good impact resistance produced from injection molding process.

SCGC™ PP P700J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process from SCG.

SCGC™ PP P701J is a homopolymer polypropylene resin suitable for general propose product produced from injection molding process

SCGC™ PP P702J is a homopolymer polypropylene resin designed for the injection molding process and suitable for general propose products that required high stiffness and good clarity.

SCGC™ PP P750J is a polypropylene resin which giving high clarity and contain anti-static agent, suitable for general propose product produced from injection molding process

SCGC™ PP P851JO is a random copolymer polypropylene resin which giving high clarity, high brightness, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC™ PP P945J is a high flow ability polypropylene impact copolymer resin. It is designed for injection molding process. This resin is recommend for product that require high impact and balance stiffness.

SCGC™ LDPE D388C is an autoclave low density polyethylene resin for extrusion coating and lamination applications. The resin offers excellent draw ability with being suitable for high speed machine.

SCGC™ LDPE D477C is an autoclave low density polyethylene resin for extrusion coating and lamination applications designed to offer good neck-in performance and high stiffness.

SCGC™ LDPE D777C is an autoclave low density polyethylene resin for extrusion coating and laminations designed to offer good processability, neck-in performance and organoleptic.

SCGC™ HDPE H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity with good toughness product.

SCGC™ HDPE H5818J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flow ability grade designed for high productivity requirement.

SCGC™ HDPE H6105JU is high stiffness and balanced impact property of high density polyethylene resin. This grade is added UV resistance suitable for industrial product produced from injection molding process.

SCGC™ HDPE H6140B is a high density polyethylene resin suitable for producing cosmetic bottles by using extrusion blow molding machine

SCGC™ HDPE S414B is a high density polyethylene resin produced by SMX™ technology. This grade can be processed at high speed blow molding machine. It is recommended for milk bottles.

SCGC™ LLDPE L1210F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE or LDPE to improve tear and seal strength.

SCGC™ LLDPE L1211FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1220F is a butene LLDPE resin with Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1221FA is a butene LLDPE resin without Slip and Antiblocking agent. It is recommended for general purpose bag with high productivity and can be blended with HDPE and LDPE to improve seal and tear strength.

SCGC™ LLDPE L1810FI is a butene LLDPE resin with high slip and antiblocking agent. It is recommended for water-quenched blown film for packaging with high clarity and good openability.

SCGC™ LLDPE L2009F is a butene linear resin with slip and antiblocking agent. It is recommended for general purpose bag with good openability and can be blended with HDPE or LDPE.

SCGC™ LLDPE L2009FA is a butene LLDPE resin without slip and antiblocking agent. It is recommended for general purpose bag with high calarity and can be blended with HDPE or LDPE.

SCGC™ PP P303S is a homopolymer polypropylene resin with high stiffness and high clarity. It is designed for sheet and solid phase pressure thermoforming products.

SCGC™ PP P348S is a special impact copolymer polypropylene base resin with high thermal stability and high impact strength at low temperature. It is designed for sheet and solid phase pressure thermoforming.

SCGC™ PP P601F is a homopolymer polypropylene resin for water-quenched blown film.This grade is contain high slip and antiblock agent and recommended for applications that film thickness is lower than 50 micron.

SCGC™ PP P602F is a Homopolymer polypropylene resin without slip and antiblock agent. This grade is recommended for water-quenched blown film for thick pakaging with excellent optical porperties and high productivity.

SCGC™ S411B is a high strength polyethylene resin designed for small blow (upto 6L) molding containers. This grade provides excellent combination of stiffness and chemical resistance for container light weighting.

Polyvinyl Chloride Homopolymer having low molecular weight, is white and free-flowing resins produced by suspension polymerization process. The resin can easily blend with variety of additives to achieve desired qualities needed in many applications. Applications are ranging from general purpose to special products regarding customer's satisfactions.

SCGC Green PolymerTM grade AP303S is a circular polypropylene homopolymer resin, the development of advanced recycling technology that turn post consumer plastic into renewable feedstock for virgin plastic resin plastic resin production

SCGC PP P951J is a random copolymer polypropylene resin which giving very high clarity, good productivity and contain anti-static agent, suitable for general propose product produced from injection molding process.

SCGC MDPE M345C is recommended to apply with primer or corona treated substrate before coating for better adhesion. The actual processing condition depends on each machine type, size, and thickness. Generally, melt temperature should be around 300-330oC

SCGC™ PP P904J is a homopolymer polypropylene resin for thin wall packaging and products with long path length.

SCGC PP P905J is a homopolymer polypropylene resin with high flowability, ultra clarity and good mechanical property balance. It is particularly designed for the injection moulding of transparent packaging.

SCGC PP P341S is an impact copolymer polypropylene with low flowability.

SCGC™ PP P304S is a homopolymer polypropylene resin with good process ability and good mechanical properties. It is particularly designed for sheeting and thermoforming products required good stiffness stability, toughness property and clarity.

SCGC SOLUTIONS

Industrial Packaging

Food and Beverage Container

Storage and Container