close

GRADE

H624WC

SCGC™ HDPE H624WC is a black bimodal high density polyethylene compound for jacketing of fiber optic and power cable applications. Its MFR and density are outer the traditional range which provide better processability, and also contains appropriate level of additives and well-dispersed carbon black to ensure excellent weathering resistance

Properties Test Methods Value Unit
Melt Flow Rate at 190 °C and 2.16 kg ASTM D 1238 0.64 g/10 min
Density (Compound) ASTM D 1505 0.960 g/cm³
Tensile Strength at Break (50 mm/min) ASTM D 638 31 MPa
Elongation at Break (50 mm/min) ASTM D 638 > 800 %
ESCR (Method B, 10% Igepal, 50 °C) ASTM D 1693 > 5,000 Hours, F0